Abstract:Cordierite glass-ceramics usually begin to crystallize from the surface. As an efficient nucleating agent, TiO2 can promote the rapid transformation of glass to bulk crystallization, but it is easy to cause the increase of dielectric constant and light absorption. High crystallinity cordierite glass-ceramics were prepared by optimizing the heat treatment process without or with different nucleating agents in stoichiometric cordierite glasses. The results show that the crystallization mechanisms of glasses without and with ZrO2+P2O5 as nucleation agents are controlled by surface crystallization. While, the glass with TiO2+ZrO2+P2O5 as nucleation agents have the tendency to be bulk crystallization. The studied glasses are crystallized from surface and have different crystallization orientations with the inner glass. The thickness of crystalline layer increased with the increasing of heating temperatures, but the "surface-center" crystallization process cannot complete by further increasing heating temperatures because of softening deformation of glasses. At 1020 ℃, the glasses complete the "surface-center" crystallization for long durations. The glasses without nucleation agents and with ZrO2+P2O5 require 10 h, but the glass with TiO2+ZrO2+P2O5 complete for 5 h. Although all the three glasses complete the "surface-center" crystallization, the glasses with nucleation agents show the higher crystallinity upon the same heat treatments. Finally, glass-ceramics with excellent performance were obtained, for example, the Z1# glass-ceramic have the high microhardness ∼7.4 GPa, low thermal expansion coefficient ∼1.4☓10−6 ℃-1 at 20–300 ℃, and relatively high thermal conductivity ∼2.4 W/mK. It also exhibits low dielectric constant and loss, which was ∼4.5 and ∼1.2☓10-3 at 1 MHz, ∼ 4.9 and 2.3☓10-3 at 10.5 GHz..

The mechanism of the crystalline characteristics of spinel-induced epitaxial growth of diopside in CMAS glass-ceramics

Catalytic mechanism of iron oxide doping on the crystallization process of Cr2O3-containg glass ceramics

Skeletal morphologies and crystallographic orientations of olivine, diopside and plagioclase

Effects of CeO<sub>2</sub> and nano-ZrO<sub>2</sub> agents on the crystallization behavior and mechanism of CaO–Al<sub>2</sub>O<sub>3</sub>–MgO–SiO<sub>2</sub>-based glass ceramics*

Crystallization And Mechanical Properties Of Spodumene-Diopside Glass-Ceramics

Preparation of Glass-Ceramics by Reactive Crystallization with Waste Glass and Mullite

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

Studies on the crystallization dynamics o Ca-P-Si glass-ceramic

Crystallization Kinetics and Mechanism of Low-Dielectric, Low-Temperature, Cofirable CaO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>Glass-Ceramics

Interface Effects on Crystal Growth and Li Ion Dynamics in Sulfide Glass-Ceramics

Influences of additives on crystal multiformity and composition in a CaO–Al2O3–MgO–SiO2–based glass–ceramics

Crystallization behavior and structure of CaO–MgO–Al2O3–SiO2 glass ceramics prepared from Cr-bearing slag

Insight into the structure and crystallization of SiO2-Al2O3-P2O5-Na2O-MgO-CaO glass system with Mg-Ca substitution: A molecular dynamics study

Epitaxial growth and interface of (1 1 1)-oriented spinel Li0.5Fe2.5O4 film on SrTiO3(0 0 1) substrate

Crystallization and Luminescence Properties of Eu 2+ Doped Diopside Glass Ceramics

Epitaxial Growth of (1 1 1)-Oriented Spinel CoCr$_2$O$_4$/Al$_2$O$_3$ Heterostructures

Crystallization mechanisms of cordierite glass-ceramics with “surface-center” crystallization behavior

Kinetic analysis of the crystallization of Y2O3 and La2O3 doped Li2O-Al2O3-SiO2 glass

Microstructure and crystallization behavior of Na2O-Al2O3-SiO2 glass-ceramics with MgO additions

Characterization of structure and properties of MgO-Al2O3-SiO2-B2O3-Cr2O3 glass-ceramics