Abstract:Carbon nanotube/continuous carbon fiber reinforced poly(ethylene terephthalate) (CNT/CCF/PET) composites are prepared by melt impregnating. The effects of CF and CNT content on the mechanical properties, melt and crystallization behaviors, and submicroscopic morphology of CNT/CCF/PET composites are studied. The tensile test results show that the increase of CF and the addition of appropriate amount of CNT improved the tensile strength and tensile modulus of the composites. When the content of CNT is 1.0 wt% and the content of CF is 56 wt%, the properties of the composites are the best, with tensile strength of 1728.7 MPa and tensile modulus of 25.1 GPa, which is much higher than that of traditional resin matrix composites. The results of dynamic mechanical analysis (DMA) show that the storage modulus of the composites increased with the increase of CF and CNT content. In particular, the addition of CNT greatly reduced the loss modulus of the composites. Morphological analysis show that the addition of CNT improved the fiber–matrix interface of the composite, which changes from fiber pull-out and fracture failure to fiber matrix fracture failure, and the fiber matrix interface is firmly bonded. In addition, there are polymer coated CNT protrusions on the surface of the fiber was observed. The results of differential scanning calorimetry (DSC) show that the melting temperature and crystallization temperature of the composites increased with the increase of CF content. The addition of CNT had little effect on the melting temperature of the composites, but it further improved the crystallization temperature of the composites. The effect of CNT content on the crystallization kinetics of the composites is studied. The non-isothermal crystallization kinetics of the composites is described by Jeziorny's improved Avrami equation. The results show that CNT has a great influence on the crystallization type of the composites. As a nucleating agent, CNT has obvious heterogeneous nucleation effect in the composites, which improves the crystallization rate of PET.

Morphology and mechanical properties of HDPE/PA66 in-situ fiberized reinforcing composites

In-situ Synthesis, Thermal and Mechanical Properties of Biobased Poly(ethylene 2,5-Furandicarboxylate)/montmorillonite (PEF/MMT) Nanocomposites

Rheological Properties of PET/PA66/Liquid Crystalline Copolyesteramide Blends

Filled Polyolefin Composites Prepared From In-Situ Polymerization Via A Catalyst-Supported Approach - I. Morphology Of Pe In Carbon Black(Cb)/Pe In-Situ Composites

Morphology and mechanical properties of poly(ether-imide)-modified polycyanurates

The study on microstructure and mechanical properties of multi-component composite based on HDPE

Mutual Nucleating and Crystallization Behavior of Poly (ethylene Terephthalate)/polyamide 66 Blends

Mechanical Properties of Injection Molded PP/PET-Nanofibril Composites and Foams

Preparation of High-Modulus and High-Strength Poly(Ethylene-Terephthalate) Fiber by Zone Annealing

Characterization and Application to Fiber Reinforced Composite of Catechol/polyethyleneimine Modified Polyester Fabrics by Mussel-inspiration

Reuse polyester/cotton blend fabrics to prepare fiber reinforced composite: Fabrication, characterization, and interfacial properties evaluation

Study on the injection-molding blends of PET and LCP

Mechanical Properties, Melting and Crystallization Behaviors, and Morphology of Carbon Nanotubes/Continuous Carbon Fiber Reinforced Polyethylene Terephthalate Composites

Influences of isothermal annealing post‐treatment on mechanical performances in fused deposition modeling manufactured short carbon fibrous PETG and PA composites

In-Situ Bubble Stretching Assisted Melt Extrusion for the Preparation of HDPE/UHMWPE/CF Composites

High Density Polyethylene Composites Reinforced with Hybrid Inorganic Fillers: Morphology, Mechanical and Thermal Expansion Performance

Fracture toughness and failure behavior of CF/epoxy composites interleaved with melt‐infused PET, PEI, and PEEK film

Evaluating fresh and hardened properties of mortar composite with different types of modified polyethylene terephthalate (PET) materials as additives: Modification effects, surface properties, shape factors

Enhancement in the Mechanical Properties of in Situ Microfibrillar PLA/POE Composites

Effects of fabrication method of composite yarn intermediate material and resin melt viscosity on the impregnation properties and mechanical properties of PA66 fiber and glass fiber composites

MORPHOLOGICAL EVOLUTION AND VISCOELASTIC BEHAVIOR OF COMPATIBILIZED HDPE/PA6 BLENDS