Refining Ti 2 AlC in the liquid region and improving the microstructure and mechanical properties of Ti-46Al-8Nb-2.6 C alloy by adding Y
Hongze Fang,Kexuan Li,Ruirun Chen,Hongyuan Zhai,Xianfei Ding,Yongchun Zou,Jingjie Guo
DOI: https://doi.org/10.1016/j.jallcom.2024.173799
IF: 6.2
2024-02-08
Journal of Alloys and Compounds
Abstract:To reveal the refinement mechanism of Ti 2 AlC particle by in-situ Y 2 O 3 in the liquid region and the improvement mechanisms of refined Ti 2 AlC in solid-state phase transformation process, Ti-46Al-8Nb-2.6C- x Y alloys were prepared. Microstructures were observed by SEM, XRD and TEM, and the mechanical properties were examined. Calculated results indicated that the phase boundary energy of in-situ Y 2 O 3 combined with TiC was low in the liquid region. TiC particle was formed initially, followed by Y 2 O 3 particle. The Y 2 O 3 particle moved to the surface of TiC particle to inhibit its growth, which left small-sized TiC nucleation substrate for the formation of Ti 2 AlC. The orientation relationship was [2̅200]Ti2AlC//[06̅6]Y2O3 . A stepped atomic diffusion zone was formed in the interface of Y 2 O 3 and Ti 2 AlC to inhibit lateral and longitudinal growth of Ti 2 AlC. As Y increased from 0.02 to 0.1 at. %, the average aspect ratio of Ti 2 AlC particles decreased from 7.7 to 3.4, the Ti 2 AlC content with the aspect ratio of 1-5 increased from 13.7 to 91.3%. The lamellar colony size and lamellar spacing reduced from 47.5 to 26.0 μm and 0.74 to 0.58 μm, respectively. Both Y 2 O 3 and refined Ti 2 AlC served as heterogeneous nucleation sites and inhibited the lateral thickening rate of γ lath. The Y-type YAl 2 phase was formed as Y content exceeded 0.1 at. %. The compressive strength and Vickers hardness were improved from 1801 to 2201 MPa and 443.2 to 464.5 HV, respectively. However, the subsequent decrease in strength was caused by the embrittlement of grain boundary after the precipitation of YAl 2 phase. The significant refinement of Ti 2 AlC and lamellar colony by in-situ Y 2 O 3 and the precipitation strengthening of Ti 2 AlC contributed to the mechanical properties.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering