Nano-yttrium-containing precipitates of T6 heat-treated A356.2 alloy when trace yttrium (Y less than 0.100 wt%) added

Xin-Ping Hu,Qing Wang,Henry Hu,Rui-Xin Li,Yang Zhao,Zhi-Ming Wang,Bing-Rong Zhang

DOI: https://doi.org/10.1007/s12598-020-01671-3

IF: 6.318

2021-02-06

Rare Metals

Abstract:<span class="a-plus-plus abstract-section id-a-sec1 outputmedium-all"><p class="a-plus-plus">To investigate the effect of yttrium (Y) on microstructure refinement and mechanical properties of aluminum alloy A356.2, the different trace contents of Y (0 wt%, 0.025 wt%, 0.050 wt%, 0.075 wt%, or 0.100 wt%) were introduced into the liquid alloy. The alloys were fabricated in a preheated permanent mold, and subsequently treated by a T6 heat treatment. The results of tensile testing indicate that the yield strength (YS), the ultimate tensile strength (UTS) and the elongation (El) of the A356.2 alloy are improved by the Y additions. The YS dependence on grain size for the test alloys follows the Hall–Petch equation, which gives <span class="a-plus-plus inline-equation id-i-eq1"><span class="a-plus-plus equation-source format-t-e-x">\({\text{YS}} = - 354.1 + {2875}{\text{.2}}d^{ - 1/2}\)</span></span> with a correlation of <em class="a-plus-plus">R</em><sup class="a-plus-plus">2</sup> = 0.83. As 0.050 wt% Y is added, the optimum values of the YS, UTS and El are achieved after T6 heat treatment. The secondary phases were identified by X-ray diffraction (XRD) which mainly consisted as Si, Mg<sub class="a-plus-plus">2</sub>Si and Al<sub class="a-plus-plus">3</sub>Y. The scanning electron microscope (SEM) and energy-dispersive spectrometer (EDS) analyses reveal the presence of the nano-sized Al<sub class="a-plus-plus">3</sub>Y particles on the surface of the Si phase. The A356.2 alloy with the Y addition is strengthened by the dendritic refinement, and the presence of the micron- and nano-sized Al<sub class="a-plus-plus">3</sub>Y precipitates.</p></span>

materials science, multidisciplinary,metallurgy & metallurgical engineering