Microstructure and Mechanical Properties of Nb Based Ultrahigh Temperature Alloy Directionally Solidified by EBFZM

Xi-ping GUO,Li-mei GAO

DOI: https://doi.org/10.3969/j.issn.1005-5053.2006.03.009

2006-01-01

Abstract:The microstructure and mechanical properties including room temperature fracture toughness K q, tensile strength σ b and elongation δ at 1250° of the Nb based alloy directionally solidified in an electron beam floating zone melting (EBFZM) furnace have been evaluated. The microstructure was primarily composed of Nb solid solution (Nbss), α-(Nb) 5Si 3 and (Nb), Si phases. After directional solidification with the moving rate of electron beam gun R being respectively 2.4, 4.8 and 7.2 mm/min, the primary Nbss dendrites, Nbss + (Nb) 5Si 3/(Nb) 3Si eutectic colonies (lamellar or rod-like) and separated Nb silicide plates aligned along the longitudinal axes of the specimens. When R = 2.4 mm/min, the best directional microstructure was obtained. Both of the tensile strength σ b at 1250°C and room temperature fracture toughness K q were improved significantly by the directional solidification. The maximum σ b incurred for the specimens with R = 2.4 mm/min and was about 85.0 MPa, meanwhile, the K q was about 19.4 MPa·m 1/2.