Influences of Mg and RE on the Microstructure and Properties of Cu-Fe-P Alloy

ZHANG Yu-tian,ZHANG Man,FU Peng-huai

DOI: https://doi.org/10.3969/j.issn.0254-6051.2006.z1.020

2009-01-01

Abstract:Optimization on composition and micro-alloying experiments were carried out on the Cu-Fe-P ally for frame castings.The influences of Mg and RE additions on the structure and the properties during deformation ageing were analyzed.Result showed that by addition of Mg and reduction of the P content,the as cast structure was compose by matrix α-Cu and coarse network sub-structure,the metallic compound,was obtained.After dissolution treatment network structure mainly disappeared instead the coarse grain with fine grain boundary of supersaturated solid solute matrix with small amount of thermo stable phases.A new phase Mg3P2 and dispersed particles would deposit from solid solution after deformation ageing.It was found that with the increase of Mg content the second phase would increase that would affect the properties of alloy after ageing treatment.