Effects of RE/V/Ti Multi-Modification on Grain Refinement of High Silicon Cast Steel

CHEN Xiang,LI Yan-xiang

DOI: https://doi.org/10.3969/j.issn.1009-6264.2006.03.017

2006-01-01

Abstract:The effects of RE,V and Ti modification on the grain refinement of high silicon cast steels(HSCS) were investigated systematically.The experiment results show that a large a mount of compounds with high-melting point is formed in HSCS after modification.Those high-melting point compounds are very effective in prompting heterogeneous nucleation of austenite and refining the austenite grain of HSCS.At the same time,the addition of modifier increases the degree of supercooling of the steel prompting nucleation of austenite and refining the grains.By modification,the dendrite grain turns into the equiaxed grain after austempering heat treatments.The volume fraction of blocky retained austenite of HSCS decreases remarkably from 31.9% without modification to 5.5% after RE/V/Ti multimodification,and the size of blocky retained austenite also decreases.