Effect of yttrium addition on dynamic mechanical properties, microstructure, and fracture behavior of extrusion-shear ZC61 + xY (x = 0, 1, 2, 3) alloys
Zhi Wang,Sheng Yao,Gengsheng Cao,Pingli Mao,Feng Wang,Le Zhou,Zheng Liu
DOI: https://doi.org/10.1016/j.matchar.2020.110615
IF: 4.537
2020-11-01
Materials Characterization
Abstract:<p>In this study, extrusion-shear ZC61 + xY (x = 0, 1, 2, 3) magnesium (Mg) alloys were prepared by a novel severe plastic deformation method, i.e., extrusion-shear, which integrates direct extrusion with equal channel angular pressing. The effect of yttrium (Y) addition on dynamic mechanical properties, microstructure, and fracture behavior of ZC61 + xY (x = 0, 1, 2, 3) alloys was investigated by Split-Hopkinson Pressure Bar setup under a strain rate of 2100 s<sup>−1</sup> along extrusion direction. With the increase in the content of added Y from 0 to 3 wt%, due to the strengthening of secondary phases and grain refinement, the yield strength of Mg alloys was enhanced from 142 to 342 MPa, and the ultimate compression strength of Mg alloys was improved from 582 to 701 MPa. During dynamic compression, the <c + a > pyramidal slip and extension twinning were the dominant deformation modes, which coordinated plastic deformation of ZC61 + xY (x = 0, 1, 2, 3) alloys. Analysis of the fracture behavior of four Mg alloys samples indicated that the fracture mode of ZC61 alloy was the brittle and melt mixed-mode; however, the fracture behavior of ZC61 + xY (x = 1, 2, 3) alloys was the brittle and ductile mixed fracture. With the increase of Y content from 1 to 3 wt%, the absorption energy density was observably increased, which was mainly responsible for the change of fracture mode from brittle fracture to ductile fracture.</c + a ></p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing