Abstract:Bioceramic hydroxyapatite/sodium titanate coating on sandblasted titanium substrate was fabricated by a three-step process. At first, the sandblasted titanium substrate was coated with a flake-like sodium titanate layer by alkali-heat treatment. In the second step, the alkali-heat treated titanium substrate was hydrothermal treated at 180 °C for 4 h with calcium solutions. In the third step, the hydroxyapatite (HA) coating was deposited onto the hydrothermal treated layer via electrochemical deposition method. The surface topography and roughness of the coatings were determined by field emission scanning electron microscope (FESEM) and a mechanical contact profilometer, respectively. The surface compositions were evaluated by X-ray diffraction (XRD), energy-dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). The EDS, XPS, and XRD analysis confirm the presence of element Ca, Ca2+, and CaTiO3 on sodium titanate layer after hydrothermal treatment with Ca(NO3)2 solution, respectively. FESEM micrograph shows the rod/needle-shaped crystallites are highly densely packed on the calcium-ion-containing layer with an average size of ~50 nm in diameter. The results indicate that the sodium titanate layer containing Ca2+ ions possesses higher ability to induce HA formation compared with the pure sodium titanate layer. It is revealed that surface composition plays an important role in the electrochemical deposition of HA. The calcium-ion-containing layer probably makes the nucleation of HA easy and effectively promotes orientated growth of HA on flake-like sodium titanate surface. The sodium titanate layer possesses a lower corrosion current density and a higher corrosion potential than sandblasted-Ti substrate. The sodium titanate layer should act as a barrier to the release of metal ions from metallic substrate to physiological solutions and thus reducing the electrochemical reaction rate.

Influence of heat treatment on the HA growth on surface of pure Ti

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

A Comparative Study of in Vitro Apatite Deposition on Heat-, H(2)O(2)-, and NaOH-treated Titanium Surfaces.

Bioactive treatment of titanium surface using a H2O2/HCl solution

Hydrothermal treatment of Ti surface to enhance the formation of low crystalline hydroxyl carbonate apatite

The Effect of Heat Treatment on Bone-Bonding Ability of Alkali-Treated Titanium

Effect of heat-treatment atmosphere on the bond strength of apatite layer on Ti substrate

Ion beam treatment of titanium surfaces for enhancing deposition of hydroxyapatite from solution

Alkali-Heat Treatment of A Low Modulus Biomedical Ti-27nb Alloy

Preparation and biological evaluation of Nano-HA coating on tatinium surfaces

Hydroxyapatite-coated Ti-6Al-4V part 2: the effects of post-deposition heat treatment at low temperatures

Effects of acid-alkali treatment on bioactivity and osteoinduction of porous titanium: An in vitro study

Topography and nanostructural evaluation of chemically and thermally modified titanium substrates

Impact of post-heat-treatment on the surface-roughness, residual stresses, and micromorphology characteristics of plasma-sprayed pure hydroxyapatite and 7%-Aloxite reinforced hydroxyapatite coatings deposited on titanium alloy-based biomedical implants

Bioactive Performances of Surface Modification of Ti–6Al–4V Jointly Using Ultrasonic‐Assisted Microarc Oxidation and Hydrothermal Treatment

Preparation of Bioactive Hydroxyapatite on Pure Titanium

One-step Modification of Nano-Hydroxyapatite Coating on Titanium Surface by Hydrothermal Method

Effect of hydrothermal treatment temperature on the hydroxyapatite coatings deposited by electrochemical method

Effect of Heat Treatment of Nano-Hydroxyapatite Coatings Prepared Using Electrohydrodynamic Deposition

Preparation of Layered Bioceramic Hydroxyapatite/Sodium Titanate Coatings on Titanium Substrates Using A Hybrid Technique of Alkali-Heat Treatment and Electrochemical Deposition

Biomimetic Deposition of Hydroxyapatite by Mixed Acid Treatment of Titanium Surfaces