Abstract:The (1−x)ZnWO4–xTiO2 composite ceramics were synthesized by the conventional solid-state method. The phase formation, microstructures, element composition and microwave dielectric properties of (1−x)ZnWO4–xTiO2 composite ceramics and 0.75ZnWO4–0.25TiO2 ceramics with Li2CO3–H3BO3 addition were investigated. Biphase structure of (1−x)ZnWO4–xTiO2 composite ceramics sintered at 1160°C/2h was confirmed by using X-ray diffraction and the back scattering electron images. The dielectric constant εr and the temperature coefficient of resonant frequency τf values of composite ceramics increased linearly with the increase of TiO2 phase. The τf value of (1−x)ZnWO4–xTiO2 was found to be dependent on phase composition, which is related to the amount of TiO2. When x is 0.25, the τf value of (1−x)ZnWO4–xTiO2 was near 0ppm/°C. With small amount of Li2CO3–H3BO3 addition, the sintering temperature of composite ceramics was further reduced to below 950°C from about 1100°C without obviously deteriorating the microwave dielectric properties, and the τf values could be adjusted with the Li2CO3–H3BO3 content. The 0.75ZnWO4–0.25TiO2 ceramics with 5.0wt% Li2CO3–H3BO3 sintered at 950°C/2h exhibited good microwave dielectric properties of εr=18.99, Q×f=13,517GHz and τf=−11.44ppm/°C.

Phase-transformation and Low-temperature Sintering of WO_3 and B_2O_3 Doped Zinc Titanate Ceramics

Phase transitions of low-temperature sintering tungsten-doped ZnO-TiO 2 ceramics

Low-temperature sintering and phase transition of zinc titanate ceramics with V2O5 and B2O3 addition

PHASE TRANSITION OF VANADIUM AND TUNGSTEN DOPED ZINC TITANATE DIELECTRIC CERAMICS BY LOW-TEMPERATURE SINTERING

Effects of WO3 Additions on the Phase Structure and Transition of Zinc Titanate Ceramics

Effects of Starting Materials and V2o5 Additions on Low-Temperature Sintering and Dielectric Properties of Zinc Titanate Ceramics

Effects of V 2 O 5 addition on the phase-structure and dielectric properties of zinc titanate ceramics

Preparation and dielectric properties of B2O3–Li2O-doped BaZr0.35Ti0.65O3 ceramics sintered at a low temperature

Effects of V<sub>2</sub>O<sub>5</sub> addition on the phase-structure and dielectric properties of zinc titanate ceramics

Dielectric Properties And Low-Temperature Sintering Of The Ba0.6sr0.4tio3 Ceramics With B2o3/Cuo Additions

Low Temperature Sintering and Dielectric Properties of BaTi_(0.75)Zr_(0.25)O_3 Ceramic

Effect of ZnO-V2O5Co-doping on phase stability and microwave dielectric properties of ZnTiO3 ceramics

Microwave Dielectric Properties of Low Temperature Sintered ZnWO4–TiO2 Composite Ceramics

Effect of ZnO-V2O5 Co-Doping on Phase Stability and Microwave Dielectric Properties of ZnTiO3 Ceramics

Effects of CuO Addition on the Structure and Electrical Properties of Low Temperature Sintered Ba(Zr,Ti)O3 Lead-Free Piezoelectric Ceramics

Structure and Microwave Dielectric Properties of Low-Temperature Sintered ZnO-TiO2 Ceramics

Phase composition and microwave dielectric properties of low firing (Zn0.8Sn0.2)TiO4 ceramics

Low Temperature Sintering Kinetics and Microwave Dielectric Properties of BaTi5O11 Ceramic

Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition

Low-temperature Sintering and High-Frequency Dielectric Properties of ZTS Ceramics with V 2 O 5 –B 2 O 3 Addition

Electrical characteristics and low-temperature sintering of BiFeO3-modified Pb(Zr,Ti)O3–Pb(Fe2/3W1/3)O3–Pb(Mn1/3Nb2/3)O3 ceramics with ZnO addition