Microstructure dependence of the electrical properties of (Ba,Sr)TiO 3 thin film deposited on (La,Sr)MnO3 conductive layer

Jun Miao,Lixin Cao,Jie Yuan,Weiran Chen,Hao Yang,Bo Xu,Xianggang Qiu,BaiRu Zhao
DOI: https://doi.org/10.1016/j.jcrysgro.2004.11.406
IF: 1.8
2005-01-01
Journal of Crystal Growth
Abstract:(00l)-oriented Ba0.7Sr0.3TiO3 (BST)/La0.67Sr0.33MnO3 (LSMO) heterostructures were deposited on (001) LaAlO3 substrates by pulsed laser deposition. We found that both the crystallinity and grain size of the BST films increased with increasing deposition temperature from 550 to 850°C. The ferroelectric properties of the BST/LSMO heterostructures were also enhanced by increasing the deposition temperature, while the largest remnant polarization and saturation polarization were 2.6 and 9.1μC/cm2, respectively. Correspondingly, the dielectric constant (zero bias) increased from 592 to 852 and the dielectric tunability (220kV/cm) increased from 9.61 to 39.3%, which may be attributed to the better crystallinity and larger grain size of the BST films. As for the current–voltage characteristics of the BST/LSMO heterostructures, the leakage current was higher for the larger grain sizes. Further study on the leakage current induced by grain size was carried out as well.
What problem does this paper attempt to address?