Optimizing the microstructure and mechanical behaviors of bimodal Mo-Si-B alloy by heat treatment
Rui Li,Xuan Chen,Bin Li,Juan Wang,Tao Wang,Fuxue Yan,Guojun Zhang
DOI: https://doi.org/10.1016/j.ijrmhm.2020.105374
IF: 4.804
2021-01-01
International Journal of Refractory Metals and Hard Materials
Abstract:<p>Previous studies revealed that developing bi-modally structured α-Mo grains in the fine-grained Mo-12Si-8.5B-0.57 wt% La<sub>2</sub>O<sub>3</sub> alloy could improve room-temperature fracture toughness without sacrificing strength dramatically. However, the toughness is expected to be enhanced further for engineering application of alloy. Here, the optimization of the bimodal α-Mo microstructure was achieved by annealing treatment at 1700–1800 °C. After annealing, the semi-continuous or isolated α-Mo colonies were transformed into the continuous α-Mo matrix meanwhile the volume fraction of α-Mo was improved slightly. Besides, the fine-grained and coarse-grained regions were coarsened concurrently and the distribution of them became more homogenous. The 1800 °C-annealed bimodal alloy exhibited an optimal microstructure consisting of dispersive Mo<sub>3</sub>Si/Mo<sub>5</sub>SiB<sub>2</sub> (~1.72–2.00 μm) particles distributed in a continuous bimodal fine-grained (~2.03 μm)/coarse-grained (~6.36 μm) α-Mo matrix. Also, this alloy presented a significantly improved fracture toughness (13.41 MPa·m<sup>1/2</sup>) and high compression strength (2682 MPa) and hardness (841 HV) simultaneously. Toughening mainly originated from crack trapping in the coarsening bimodal α-Mo structure and forming intragranular micro-cracks in the coarsening α-Mo and intermetallic phases induced by La<sub>2</sub>O<sub>3</sub>. High compression strength was attributed to the coarseness of α-Mo phase improving the plastic deformation capacity of alloy.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering