Abstract:2.25Cr-1Mo-0.25 V steel has been widely used to manufacture hydro-processing equipment operating under harsh environments for its good creep performance. Warm bending, a common fabricating process of 2.25Cr-1Mo-0.25 V steel ring shells, inevitably changes the creep property of 2.25Cr-1Mo-0.25 V steel, but its detailed effect still remains obscure. In this work, we experimentally investigated the impact of warm bending on the microstructure and creep behavior of 2.25Cr-1Mo-0.25 V steel. First, a series of creep rupture tests were carried out at 482 °C and 350 MPa, in which test materials were extracted from an actually fabricated ring shell and its raw plate. Thereafter, the microstructures of test materials were semi-quantitatively analyzed by various characterization techniques, such as electron backscatter diffraction (EBSD) and three-dimensional high-resolution X-ray computed tomography (3D μ-XCT). Finally, warm forming induced microstructural degradation as well as their implication for creep was discussed in detail. Creep rupture tests showed that warm bending leads to a significant decrease in creep lifetime at the surface region of virgin plate but a slight decline at the central region of virgin plate. An inhomogeneous creep resistance distribution was thereby revealed along the thickness direction of the ring shell, which could not be completely eliminated by subsequent tempering at 705 °C for 8 h. Moreover, microstructural observations demonstrated that warm deformation leads to multiple microstructural deterioration, including carbide coarsening, ferrite matrix softening, void defect increasing, etc. Their combined action appears to accelerate the creep fracture behavior of 2.25Cr-1Mo-0.25 V steel. This work will contribute to the long-term safety and integrity assessment of 2.25Cr-1Mo-0.25 V steel structures. Graphical abstract

On the creep fracture toughness of 21/4Cr1Mo steel

On the Creep Fracture Toughness of 2¼cr1mo Steel

ON THE TIME-DEPENDENT MATERIAL FRACTURE TOUGHNESS AT HIGH TEMPERATURE

Creep fracture toughness of welded joint for 2.25Cr1Mo steel

Effect of constraint on creep fracture toughness of a Cr-Mo-V steel

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Revealing influence of warm bending on creep performance of heat-resistant 2.25Cr-1Mo-0.25 V steel

Low cycle fatigue and creep-fatigue interaction behavior of 2.25CrMoV steel at high temperature

Evaluation of the time dependent failure assessment curves for 10CrMo910 and 316 SS at 550°C

The Effect of CT Specimen Thickness on High Temperature Creep Crack Growth Rate of 25Cr2NiMo1V Steel

Creep Crack Growth in A Cr-Mo-V Type Steel: Experimental Observation and Prediction

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Creep Behavior and Cavitation Evolution of 15crmog Steel at High Temperatures

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Effect of the Out-Of-Plane Constraint on Creep Crack Growth Property of Cr-Mo-V Type Steel

Safety assessment method for defective structures in creep regime

Study on the High Temperature Creep Behavior of 30Cr25Ni20 Heat-Resistant Steel

Experimental Investigation Of In-Plane Constraint And Out-Of-Plane Constraint Effects On Creep Crack Growth

Creep Property Evaluation of a 2.25cr–1mo Low Alloy Steel

Creep behavior analysis on ruptured welds of heat-resistant steels with two different failure modes

Time-dependent Failure Assessment Diagram for Integrity Assessment of Defective Structure at Elevated Temperature