Creep Property Evaluation of a 2.25cr–1mo Low Alloy Steel

S. -H. Song,J. Wu,X. -J. Wei,D. Kumar,S. -J. Liu,L. -Q. Weng

DOI: https://doi.org/10.1016/j.msea.2010.01.007

2010-01-01

Abstract:The creep properties of a 2.25Cr–1Mo steel which was quenched from 1253K and tempered at 923K were examined under different engineering stresses (225–325MPa) at temperatures ranging from 773 to 898K. The creep behavior followed the temperature-compensated power law and Monkman–Grant equations. In the temperature-compensated power law equation, the apparent activation energy and stress exponent for creep were determined as approximately 380kJ/mol and 10, respectively. In the Monkman–Grant relation, the values of m and C were determined as around 1.016 and 0.0528, respectively, when the minimum creep rate was in h−1 and the rupture time in h. In all conditions considered the specimens all presented ductile fracture with a rupture strain over 29%. There existed a minimum value of rupture strain at 250MPa as the rupture strain varies with applied stress from 225 to 325MPa when testing at 823K, which could be caused by recrystallization in the fracture tip areas of the material.