Phase transformation in the Al2O3–ZrO2 system
L Gao,Q Liu,J. S Hong,H Miyamoto,S. D De La Torre,A Kakitsuji,K Liddell,D. P Thompson
DOI: https://doi.org/10.1023/A:1004327104481
IF: 4.5
1998-01-01
Journal of Materials Science
Abstract:Co-precipitation methods have been used to produce 20 mol% Al2O3–80 mol% ZrO2 mixed oxides, from aqueous solutions of zirconium oxychloride and aluminium chloride, followed by precipitation with ammonia. The resulting gel was calcined at increasing temperatures, and X-ray diffraction confirmed that the structure remained amorphous up to 750°C and then crystallized as a single-phase cubic zirconia solid solution, but with a reduced unit-cell dimension. At higher temperatures, the unit-cell dimension increased and, above 950°C, this phase started to transform to a tetragonal zirconia (t-ZrO2) phase, again of reduced cell dimensions compared with t-ZrO2, with simultaneous appearance of small amounts of θ-Al2O3. Above 1100°C, the tetragonal phase transformed to monoclinic zirconia on cooling, and the amount of θ-Al2O3 increased. Above 1200°C, the θ-Al2O3 transformed to the stable α-Al2O3. These results confirm that aluminium acts as a stabilizing cation for zirconia up to temperatures of about 1100°C. © 1998 Chapman & Hall