Preparation and Tribological Properties of Monodispersed Metallic Cu-Sn Alloy Nanoclusters with Modified Surface
Tao Zhao,Shuhui Yuy,Zhijun Zhang,Rong Sun,Ruxu Du
DOI: https://doi.org/10.1007/978-3-642-03653-8_304
2009-01-01
Abstract:Recently, the di-n-octodecyldithiophosphate (DDP) coated nanoparticles such as MoS2[1], ZnS[2] and Cu[3] used as oil additives have been investigated, results showed these coated nanoparticles exhibited good tribological properties. Cu nanoparticle have also attracted considerable attention because of their catalytic, optical, conductive[4-7]. A number of different ways have been developed to prepare Copper nanoparticles, such as thermal reduction[4], microemulsion[8], sonochemical reduction[9], and chemical reduction[10]. Thereinto, the liquid phase chemical reduction method[11-14] has proved the most versatile and simple approach for nanomaterials because of the controlled expediently nucleation and growth. In this study, monodispersed Cu-Sn alloy Nanoclusters were prepared in the water/acetone system. The nanoclusters were characterized with XPS, FT-IR, TG, TEM and ED. The friction experiments were carried out with the MRS-10A four-ball testing machine under a rotating speed of 1450 rpm in the ambient conditions. The employed base oil was Chang Cheng lubricants (SE 15W/40). The contents of the additives were in the range of 0.25-1.0% by weight. The results indicate that the Cu-Sn nanoclusters have small kinetic friction coefficient and shows lubrication and anti-wear property. The friction and wear mechanism of the nanoclusters in oil was also discussed. Based on the results of surface analysis, the action mechanisms of the Cu-Sn nanoclusters as lubricant additives, can be described as: under boundary lubricating conditions, nanoclusters are transferred to the friction surface and generate a mixed boundary thin film, which simultaneously reduces the friction and wear.