Abstract:Journal of Composite Materials, Ahead of Print. Post-curing cycles have an effective impact on the thermal and mechanical properties of thermoset composite materials. Typically, post-cure cycles use heat to expose cured resin parts to high temperatures in an attempt to maximize their final properties. In most cases, these processes allow composite parts to achieve the highest possible strength and become stable. In industrial practice, however, it has been found that there are potential consequences of performing localized repairs on composite parts in an autoclave where the localized repair undergoes a normal curing process while the parent part undergoes an additional curing process. Thus, for the parent part, prolonged exposure to high temperatures can trigger a process of decomposition of the resin matrix, as could be the aging phenomena of composites in service. In such a scenario, two practical questions are worth asking: (1) to what extent can a resin matrix be post cured without risking degrading its thermal properties? (2) what are the residual mechanical and physical properties resulting from prolonged exposure of composite parts to elevated temperatures? In this work, an analysis was carried out to estimate the potential adverse effects on thermoset composite parts made of carbon fibre and epoxy resin materials commonly used in aerospace, in terms of thermal, physical and mechanical properties after a long exposure to high temperatures caused by multiple post cure cycles. Two types of prepreg laminates were used to make monolithic test panels using twill and plain weave architectures for the M21 and 8552 test panels respectively. Thermal tests were conducted to evaluate the evolution of the degree of cure, the glass transition temperature and the inter-laminar shear strength of post-cured panels, which were subjected to a different number of post cure cycles. The study found that multiple post cure cycles alter thermal properties, which in turn have adverse effects on physical and mechanical properties. The results demonstrated that the two types of composite materials respond differently to changes in properties. Twill weave panels quickly reach full cure after three stages while plain weave panels have undergone gradual curing. This difference in the curing process of the resin matrix clearly influenced the changes in the measurements of shear, surface hardness and compressive strengths.

Investigation on low temperature curing LT-02 epoxy matrix composite

Study on Co-curing Behavior and their Laminate Properties of Low Bromined Epoxy/Cyanate Blends

Effects of the Heating Rate and the Amount of Organic Montmorillonite on the Thermal Properties of the Novel Liquid Crystalline Epoxy Nanocomposite

Size Effect in Curing Optimization for Thick Composite Laminates

Low Temperature Cure High Performance Composites

Investigation on a Novel Low Temperature/Vacuum Bag Cure Prepreg

Optimization of a high-pressure microwave curing process for T800/X850 carbon fiber-reinforced plastic

Experimental Study of Curing Temperature Effect on Mechanical Performance of Carbon Fiber Composites with Application to Filament Winding Pressure Vessel Design

Curing behavior and properties of ultra-high temperature resistant RTM bismaleimide resin

Study on the Curing Behavior of Polythiol/phenolic/epoxy Resin and the Mechanical and Thermal Properties of the Composites

Experimental research on hygrothermal properties of carbon fiber/epoxy resin composite under different hygrothermal conditions

Effects of multiple post cure cycles on properties of composite carbon fibre and epoxy materials

Effect of post-cure on the glass transition temperature and mechanical properties of epoxy adhesives

Effect of Curing Agents on Electrical Properties of Low-Temperature Curing Conductive Coatings and Thermodynamic Analysis

Preparation of low‐temperature curing single‐component epoxy adhesives with sedimentation coated accelerators

Investigation on the mold‐less curing process of 3D printing continuous carbon fiber reinforced thermoset composites based on thermoplastic shells constraint

STUDY ON PROCESS SUITABILITY OF MANUFACTURING THICK-COMPONENT USING 5428/T700 SYSTEM

On the Analyses of Cure Cycle Effects on Peel Strength Characteristics in Carbon High- Tg Epoxy/Plasma-Activated Carbon PEEK Composite Interfaces: A Preliminary Inquiry

Fast‐Curing of Liquid Crystal Thermosets Enabled by End‐Groups Regulation and In Situ Monitoring by Triboelectric Spectroscopy

Improved Melt Processabilities of Thermosetting Polyimide Matrix Resins for High Temperature Carbon Fiber Composite Applications

Study on temperature gradient of ultra-thick foam sandwich composite structure during curing