Abstract:Temperature plays an important impact on rock mechanical properties. In this paper, the mechanical properties, fracture mechanism and constitutive model of marble under 20–120 °C and 15 MPa are studied. The results show marble deformation can be divided into four stages: compaction, linear elasticity, crack propagation and post-peak failure. Stress–strain curve is not obviously affected by temperature. Macroscopic fracture characteristics change from shear failure to tensile mixed failure with temperature increasing. With the increase of temperature, the strength of marble tends to decrease, indicating that temperature increase has a weakening effect on marble, and there are temperature-sensitive areas of 20–60 °C and temperature sub-sensitive areas of 60–120 °C. The elastic modulus of marble decreases and Poisson's ratio increases with increasing temperature. The energy evolution law of marble under different temperature is basically the same, which shows that before crack initiation, the energy dissipation is less, and after the damage and yielding occurs, the energy dissipation increases quickly. The energy dissipation in the failure process is mainly used for crack initiation-connection-penetration, as well as plastic deformation caused by friction and slip of cracks, and the plastic deformation and energy dissipation have good linear characteristics. The statistical damage constitutive model based on three-parameter Weibull distribution function can effectively reflect the characteristics of post-peak plastic deformation and strain softening. The weakening effect of marble at 20–120 °C is related to its internal moisture excitation. With the increase of temperature, water is stimulated to absorb and attach to the original relatively dry interface, which plays a role in lubrication. The relative motion friction resistance between solid particles or crack surfaces decreases, which leads to crack initiation and friction energy consumption reduction, changes the specific surface energy of rocks and weakens the strength of marble. The results provide a theoretical basis for predicting and evaluating the long-term stability and safety of surrounding rock of underground deep engineering in complex environment with high ground temperature and high geo-stress.

Experimental Study on High Temperature Effect's Influence to the Strength and Deformation Quality of Marble

Experimental Study on Whole Stress-Strain Characteristic of Marble under the Action of High Temperature

TEST RESEARCH ON MECHANICAL PROPERTIES OF MARBLE UNDER HIGH TEMPERATURE

Fracture mechanism and constitutive model considering post-peak plastic deformation of marble under thermal–mechanical action

Experimental Research on Ultrasonic Characteristic of Marble under the Action of High Temperature

The Friction Angle of the Leiyang Marble Surface after Exposure to High Temperature

Experimental study on dynamic behavior of concrete at elevated temperatures

Effect of Freeze–Thaw Temperature and Number of Cycles on the Physical and Mechanical Properties of Marble

Mesoscopic and macroscopic investigation of a dolomitic marble subjected to thermal damage

Experimental Study on Mechanical and Porous Characteristics of Limestone Affected by High Temperature

Experimental study on the variation of physical and mechanical of rock after high temperature treatment

Experimental Study on Infrared Temperature Characteristics and Failure Modes of Marble with Prefabricated Holes under Uniaxial Compression

Anisotropy Response Characters of Marble After High Temperature

A novel true triaxial test device with a high-temperature module for thermal-mechanical property characterization of hard rocks

Experimental Study on Dynamic Mechanical Properties and Energy Evolution Characteristics of Limestone Specimens Subjected to High Temperature

Experimental Study on Mechanical Behaviors and Fracture Features of Coarse Marble Specimens after Thermal Shock

Temperature-dependent evolution of permeability and pore structure of marble under a high-temperature thermo-hydro-mechanical coupling environment

Mechanical Properties of Limestone After High-Temperature Treatment Under Triaxial Cyclic Loading and Unloading Conditions

The impact of high temperature on mechanical properties and behaviors of sandstone

Study on dynamic response characteristics of impact of freeze-thaw saturated marble in plateau area

Effects of high temperatures on mechanical performance of basaltic tuff and mechanism analysis