Abstract:Al-Mg-Si series aluminum alloy is a heat-treatment-strengthened alloy. Research on the impact resistance of Al-Mg-Si series aluminum alloy is of great significance to expand its application in engineering. Taking 6082-T6 aluminum alloy as the concrete research object, using the split Hopkinson pressure bar (SHPB) device, the dynamic mechanical response of the material under different temperatures and average strain rates was studied, and the service performance of the material under extreme conditions was determined. The absolute temperature rise was introduced to optimize the existing constitutive model. The results show that when the environment temperature is 298.15~473.15 K under high-speed impact, the internal thermal softening effect of the material is dominant in the competition with the work hardening, resulting in a decrease in the flow stress of the material. Through the analysis of the real stress–strain curve, it was found that the elastic modulus of the material was negatively correlated with the strain rate, negatively correlated with the temperature, and showed an obvious temperature-softening effect. Yield strength was negatively correlated with temperature and positively correlated with strain rate, which showed an obvious strain rate hardening effect. Based on SEM microscopic analysis, it was found that under given conditions, adiabatic shear bands appeared in some samples, and their internal structures demonstrated obvious change. It was judged that when high-speed impact occurs, cracks are induced at the shear bands, and the cracks will continue to develop along the adiabatic shear bands, resulting in many oblique cracks which will gradually become larger and eventually lead to material failure. Finally, based on the model, the strain rate and temperature softening terms were improved, and a rise in adiabatic temperature rise was introduced. The improved model can better describe the strain rate effect of the material and accurately describe its flow stress. It provides a theoretical basis for the engineering application of materials.

Study on the limit strain-rate softening property of Al-Li alloy

Mechanical properties of rapidly solidified Al-Ti alloys after thermal exposure

Study on Dynamic Impact Response and Optimal Constitutive Model of Al-Mg-Si Aluminum Alloy

Constitutive modeling and microstructure characterization of 2196 Al-Li alloy in various hot deformation conditions

Characterization and constitutive analysis-based crystal plasticity of warm flow and fracture behaviours of 2060 Al-Cu-Li alloy

Microstructures, hot tensile deformation behavior and constitutive modeling in a superlight Mg-2.76Li-3Al-2.6Zn-0.39Y alloy

INFLUENCE OF LOADING RATE ON Al-Li ALLOY FRACTURE TOUGHNESS

In-situ surface study on the mechanism of high-strain-rate superplasticity in an Al–Cu–Li alloy

Strain Rate Sensitivity and Adiabatic Shear Deformation of an Advanced Al-Mg Alloy

Study on Mechanical Properties and Constitutive Model of 5052 Aluminium Alloy

Dynamic Mechanical Properties and Modified Material Constitutive Model for Hot Forged Ti2AlNb over Wide Ranges of Temperature and Strain Rate

Study on the Optimization of the Tensile Properties of an Al-Li Alloy Friction Stir-Welding T-Joint

Strain Compensation of the Constitutive Equation for High Temperature Flow Stress of a Al-Cu-Li Alloy

Dynamic Softening Mechanism and an Improved Unified Constitutive Model for an Al–Cu–Mn–Fe–Zr Alloy during Warm Deformation

The Influence of Aging Precipitates on the Mechanical Properties of Al–Li Alloys and Microstructural Analysis

Research and Revise on Constitutive Equation of 7050-T7451 Aluminum Alloy in High Strain Rate and High Temperature Condition

Anisotropy in creep-aging behavior of Al–Li alloy under different stress levels: experimental and constitutive modeling

Static Softening Behavior and Modified Kinetics of Al 2219 Alloy Based on a Double-Pass Hot Compression Test

Constitutive Analysis and Microstructure Characteristics of As-Homogenized 2198 Al–Li Alloy under Different Hot Compression Deformation Conditions

Modeling of Strain Hardening Behavior and Mechanical Properties of Al 7Si Mg Cast Aluminum Alloys During Tensile Process

Origin of strain softening in a nanograined Al alloy