Hot processing performance and fracture toughness control of Al CrFeNiCu1.5 (x = 0, 0.2, 0.4, 0.6, 0.8) high entropy alloys
Shulin Dong,Rongyi Na,Yingdong Qu,Ruirun Chen,Guanglong Li,Wei Zhang,Siruo Zhang,Shibing Liu
DOI: https://doi.org/10.1016/j.mtcomm.2024.108566
IF: 3.8
2024-03-01
Materials Today Communications
Abstract:In order to develop high-entropy alloys with both good hot processing performance and fracture toughness, Al x CrFeNiCu1.5(x=0, 0.2, 0.4, 0.6, 0.8) alloys were designed and prepared. The alloy was firstly hot rolled by a twin-roll rolling device, and then the hot processing performance of the alloy under different Al contents was explored, whether the fracture toughness was at an ideal level, and if so, why it was at an ideal level. The results showed that the phase composition after hot rolling and annealing were two phases (face-centered cubic FCC and body-centered cubic BCC). With the increase of Al content, the FCC phase gradually transformed into BCC phase, and the increase of BCC phase led to the decrease of plasticity, which led to the decrease of hot processing performance. With the increase of Al content, the average fracture toughness value increased first and then decreased. Among them, the Al0.2CrFeNiCu1.5 and Al0.4CrFeNiCu1.5 alloys had the relatively better fracture toughness, which was because that the alloys had the appropriate proportion of FCC and BCC phases, and the strength and plasticity could achieve an ideal match. Among these alloys, the Al0.2CrFeNiCu1.5 alloy had the relatively better hot processing performance and ideal fracture toughness, and its average fracture toughness was 35.71 MPa·m1/2. And compared with Al0.2CrFeNiCu1.5 alloy, the Al0.4CrFeNiCu1.5 alloy had the worse hot processing performance, but it yielded the best fracture toughness, with an average value of 45.27 MPa·m1/2. In the crack propagation morphology, we found the main crack terminated at the notch upper part for the Al0.2CrFeNiCu1.5 alloy, suggesting that the material has good plasticity. And we also found crack multiple deflections and secondary cracking for the Al0.4CrFeNiCu1.5 alloy, which was helpful to improve the fracture toughness.
materials science, multidisciplinary