Abstract:Using a graphite rod with a hole filled with the powder of a mixture of Y-Ni alloy and graphite as anode; single-wall carbon nanotubes (SWCNTs) with 50%-70% purity were produced in quantity of tens of grams a day under the are conditions of 40-60 A d.c. and helium pressure of 2 arm. If calcium-nickel was used as catalyst instead of yttrium-nickel, high yields of SWCNTs can also be produced in large quantities, although the yield was slightly less than that of yttrium-nickel. The samples were characterized by SEM, HREM, and Raman spectroscopy. The results showed that the SWCNTs produced with yttrium-nickel as catalyst had the same structures as those obtained from laser-ablation with Co-Ni as catalyst. SWCNTs with smaller diameters were found when calcium-nickel was used as catalyst, proving that the diameter of SWCNTs is dependent on the properties of the metal catalysts. Furthermore, high helium pressure can lead to a high yield of SWCNTs. Our results suggested a formation mechanism of SWCNTs and the roles played by nickel and yttrium or calcium element.

Large Scale and High Purity Synthesis of Single-Walled Carbon Nanotubes by Arc Discharge at Controlled Temperatures

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Large Scale Synthesis of Single-Wall Carbon Nanotubes by Arc-Discharge Method

A Novel Method to Produce Large Amount Single-Walled Carbon Nanotubes by Arc Discharging

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

Catalyst Effect on the Preparation of Single-Walled Carbon Nanotubes by a Modified Arc Discharge

Purification of Single-Wall Carbon Nanotubes

Preparation of Large Amounts of Carbon Nanotubes in Hydrogen Atmosphere by Arc-Discharge

Purification and characterization of single-walled carbon nanotubes produced by arc-discharge

Temperature and Catalyst Effects on the Production of Amorphous Carbon Nanotubes by a Modified Arc Discharge

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Synthesis of high quality single-walled carbon nanotubes by arc discharge method in large scale

Direct Synthesis of High Purity Single-Walled Carbon Nanotube Fibers by Arc Discharge

Current and Arc Pushing Force Effects on the Synthesis of Single-Walled Carbon Nanotubes by Arc Discharge.

Production of Single-Wall Carbon Nanotubes at High Pressure

An Efficient Method to Produce Single-Walled Carbon Nanotubes by Round-Trip Arc Discharge

Purification of single-walled carbon nanotubes synthesized by the hydrogen arc-discharge method

Mass-production of single-wall carbon nanotubes by arc discharge method

Carbon Nanotubes Grown on the Surface of Cathode Deposit by Arc Discharge

Synthesis of Single-Walled Carbon Nanotube Films with Large Area and High Purity by Arc-Discharge