Preparation and aging behavior of nano SiO2 modified PEA coating by In-Situ polymerization

Haifeng Chen,Zhiyu Wang,Jianjun Chen,Xianping Fan,Gongdong Qian

DOI: https://doi.org/10.3321/j.issn:1002-185x.2004.z1.003

2004-01-01

Rare Metal Materials and Engineering

Abstract:Using the materials of TEOS, ethanol, ammonia water, we prepared the concentrated solution containing 200nm, no lump, even-distributed nano SiO2 particles through the modification of the Stober at the room temperature. Adopting this stable concentrated solution, we obtained the nano SiO2 modified PEA film. From the analysis of the UV-Vis spectra, we found that the nano SiO2 particles had a strong screening effect on the UV, thus it could greatly enhance the anti-aging capacity of the PEA coating under the radiation of the ultraviolet wave. Using the concentrated solution containing nano SiO2 particles as the nano-modified additive and the method of In-Situ polymerization, we obtained the nano SiO2 modified PEA exterior wall coating. According to the national standard GB/T9755-2001 aging test, the nano SiO2 modified PEA exterior wall coating obtained by In-Situ polymerization, had no sign of pulverization under the test for 1800 hours. Thus, it outperformed the demand of 600 hours of the international high-class products. Upon aging test for 1200 hours, color change was 2nd grade. Comparing with the common exterior wall coating, it extended 200 hours further, thus was much better than the national high-class product. The comparison results of aging test, showed if the nano-sized powders were directly dispersed into the additives, there was no sign of mitigating the coating's aging process; instead, it accelerated the pace of aging. Without the working procedure of filtration and sintering, the goal of nano modification could be realized by In-situ polymerization. By taking advantage of the screening effect of the nano SiO2 particles, it got rid of the weakness that directly using the nano-sized powders as the additive of the coating could not evenly disperse the nano-particles.