Abstract:In particle formation, the method can be just as important as the chemical reaction involved. A new method of synthesizing hydrotalcite-like layered double hydroxides (LDHs) of the type [Mg1-xAlx(OH)(2)](x+)(CO32-)(x/2).yH(2)O (X = 1.7-3.3) is reported. The key features of this method are a very rapid mixing and nucleation process in a colloid mill followed by a separate aging process. The properties of the resulting LDHs are compared with those of materials produced using the conventional coprecipitation process at constant pH. The compositions and structural parameters of the materials synthesized using the two routes are very similar, although the crystallinity is slightly higher for the LDHs produced using the new method. The thermal behavior of the materials synthesized using the two routes is also similar. The major advantage of the new method is that it affords smaller crystallites with a higher aspect ratio, having a very narrow distribution of crystallite size. In the conventional coprecipitation process at constant pH, the mixing process takes considerable time such that nuclei formed at the beginning of the process have a much longer time to undergo crystal growth than those formed at the end of the process. The consequence is that a wide dispersion of crystallite sizes is obtained. In the colloid mill process, however, the mixing and nucleation are complete in a very short time and are followed by a separate aging process. Furthermore, we suggest that the extreme forces to which the nucleation mixture is subjected in the colloid mill prevent aggregation of the nuclei and result in the nuclei having a uniform small size. When the resulting mixture is aged in a separate process, well-formed crystallites with a similarly narrow range of diameters result.

Preparation of Acicular Nanocrystalline Mg,Al-hydrotalcite by Liquid Method

Effect of the Na; CO; concentration on the preparation of hydrotalcite

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Influence of Different Al Resources and Preparation Methods on the Synthesis of Mg-Al Hydrotalcite-like Compounds

Synthesis of High-Crystallinity Mg-Al Hydrotalcite with a Nanoflake Morphology and Its Adsorption Properties for Cu2+ from an Aqueous Solution

Preparation Of Layered Double-Hydroxide Nanomaterials With A Uniform Crystallite Size Using A New Method Involving Separate Nucleation And Aging Steps

Influence of different raw materials on the crystal structure and morphology of Mg-Al-CO_3 hydrotalcite

Preparation of Magnesium Aluminum Hydrotalcite with Orderly Porous Structure by Colloidal Crystal Template

Synthesization and Characterization of Mg, Al- Hydrotalcites

Study of the Effects on Synthesis Mg-Al-hydrotalcite-like Compounds

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Studies on Preparation and Crystal Structure of Ultrafine Particles Zn-Mg-Al-Hydrotalcite-like Compound

The low temperature preparation of nanocrystalline MgAl2O4 spinel by citrate sol–gel process

The Co-Precipitation Preparation and Properties of Inorganic Hydrotalcite

Synthesis and Characterization of MgAl-hydrotalcite and Its Intercalation Assembled Compound

Preparation and Flame Retardancy of Hydrotalcite/Montmorillonite Nanocomposite

Solid-state reaction preparation and sintering behavior of MgAl 2O 4 nanopowders

Study on Thermal Decomposition Process of MgAl-hydrotalcite

Controlled Synthesis Of Magnesium Hydroxide Nanoparticles With Different Morphological Structures And Related Properties In Flame Retardant Ethylene-Vinyl Acetate Blends

Studies on Preparation of Flame Retardant Mg(OH)2 in a Large-scale Experimental Set-up with Different Temperature

Synthesis and Hydriding/dehydriding Properties of Nanosized Sodium Alanates Prepared by Reactive Ball-Milling