Abstract:A magnesium–aluminum-layered double hydroxide (Mg-Al LDH) with a nano-lamellar morphology was prepared by using a homogeneous precipitation and hydrothermal method, and a calcination product (Mg-Al LDO) of the Mg-Al LDH was also obtained in this work. The XRD, TEM, SEM, FTIR, N2 ad/desorption, and TG-DTG techniques were employed to characterize the microstructures, morphologies, and thermostability levels of these two materials in detail. The results showed that both the Mg-Al LDH and Mg-Al LDO had mesoporous structures and nanoplate morphologies, with diameters of 50~200 nm. The Mg-Al LDH was transformed into Mg-Al LDO at 773 K in an air atmosphere. The adsorption properties of the Mg-Al LDH were investigated systematically with a copper chloride solution as a simulated waste. The experimental results demonstrated that the pH value of the solution had an obvious influence on its Cu2+ adsorption capacity, and the optimal pH value was approximately 5.0. The adsorption kinetics results showed that the Mg-Al LDH had a rapid adsorption rate, and the equilibrium adsorption capacity was 62.11 mg/g. Additionally, the Cu2+ adsorption could be commendably described using a pseudo-second-order model, demonstrating that the adsorption behavior is regulated by chemical sorption. The adsorption thermodynamic results indicated that the adsorption process was spontaneous at temperatures above 318 K. Moreover, the ΔG0 values decreased as the temperature was raised, which indicated that a higher temperature can cause a greater impetus for Cu2+adsorption. In addition, the positive values of the ΔH0 indicated that the Cu2+ adsorption was endothermic, and the positive ΔS0 values revealed an increase in the confusion at the solid–liquid interface of the adsorbent.

Study on Thermal Decomposition Process of MgAl-hydrotalcite

The Non-isothermal Kinetic Analysis of Thermal Decomposition of Mg(OH)2

Study on the non-isothermal decomposition kinetics of AlOOH coated calcium carbonate

Investigation of catalytic modification of light magnesium based hydrogen storage material

Study of the Effects on Synthesis Mg-Al-hydrotalcite-like Compounds

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Kinetic Study on the Thermal Decomposition of Layered Double Hydroxides

Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds

Achieving Both High Hydrogen Capacity and Low Decomposition Temperature of the Metastable AlH3 by Proper Ball Milling with TiB2

Effect of coprecipitation method on Mg–Al hydrotalcite properties: application in the synthesis of diethylene glycol di-(methyl carbonate)

Structural and Surface Acid/Base Properties of Hydrotalcite-Derived MgAlO Oxides Calcined at Varying Temperatures

Decomposition Processes of Organic-Anion-Pillared Clays CoaMgbAl(OH)c(TA)d·nH2O

Study on the mechanisms and kinetics of complex's thermal decomposition getting anhydrous magnesium chloride

Thermal decomposition kinetics of magnesite from thermogravimetric data

Synthesis of High-Crystallinity Mg-Al Hydrotalcite with a Nanoflake Morphology and Its Adsorption Properties for Cu2+ from an Aqueous Solution

Non-isothermal Decomposition Reaction Kinetics of the Magnesium Oxalate Dihydrate

Effect of Mg/Al molar ratio on the basicity of Mg-Al mixed oxide derived from Mg-Al hydrotalcite

An experimental study on thermal decomposition behavior of magnesite

Improved Hydrogen Storage Properties of MgH2 by Ball Milling with AlH3: Preparations, De/rehydriding Properties, and Reaction Mechanisms

Structure and Base Properties of Calcined Hydrotalcites

Adsorption of Nitrate and Nitrite from Aqueous Solution Onto Calcined (mg–al) Hydrotalcite of Different Mg/Al Ratio