Study on thermodynamic equilibrium and character inheritance of cobalt carbonate decomposition
Zhen Ouyang,Ping Wen,Yifeng Chen,Longgang Ye
DOI: https://doi.org/10.1016/j.vacuum.2020.109559
IF: 4
2020-09-01
Vacuum
Abstract:<p>Presently, the main cobalt powder production method is the reduction of cobalt carbonate, and the decomposition process significantly influences the properties of the ensuing cobalt powder. Thus, the objective of this study was to investigate CoCO<sub>3</sub> decomposition using thermodynamic simulations and calculations, as well as experiments. The results obtained led to the conclusion that in the absence of oxygen, CoCO<sub>3</sub> primarily decomposes into CoO and CO<sub>2</sub>. However, in the presence of oxygen, it preferentially undergoes oxidation decomposition, generating Co<sub>3</sub>O<sub>4</sub> and CO<sub>2</sub>, while the unreacted CoCO<sub>3</sub> subsequently decomposed forming more CoO when O<sub>2</sub> was exhausted. Additionally, Co<sub>3</sub>O<sub>4</sub> decomposed to CoO and O<sub>2</sub> at high temperatures. TG-DSC-MS analyses showed that the temperature at which CoCO<sub>3</sub> decomposed into CoO was 332 °C. The analysis of the CoCO<sub>3</sub> decomposition process performed in an inert atmosphere showed that the decomposition product, CoO was generated at temperatures above 300 °C. Furthermore, SEM results showed that the morphology of the CoO obtained depends on that of the raw material (CoCO<sub>3</sub>), and a higher temperature induced agglomeration; thus, increasing CoO size. Lower decomposition temperatures, higher gas flow rates, and lower heating rates resulted in a decrease in CoO particle size.</p>
materials science, multidisciplinary,physics, applied