Influence of the Phenol-Aldehyde Resin Structure on the Tensile Strength of Cast Products

唐黎明,胡飞,方宇,齐东超,祝建勋

DOI: https://doi.org/10.3321/j.issn:1000-0054.2004.09.004

2004-01-01

Abstract:The tensile strength of foundries was improved using three alkaline phenol-aldehyde resins prepared at pH of 14, 8 and 3 as binders in the CO_2 cold-box process. The polymer structures were characterized by IR and ~1H NMR analysis. The results showed that the resin formed at pH=14 contains a large amount of active hydroxymethyl groups with the phenyl groups linked by both ether linkages and methylene bridges. Thus, the cast product had high tensile strength with the highest initial strength of 0.64 MPa and 24 h strength of 0.80 MPa. In addition to the active hydroxymethyl groups, the resin obtained at pH=8 had very few ether linkages with the phenyl groups connected mainly by methylene bridges. As a result, the cured product has low tensile strength. The resin prepared at pH=3 has very few active hydroxymethyl groups in the molecules. The resulting product has the lowest initial tensile strength of the three samples.