Study on the Preparation and Properties of Colored Iron Oxide Thin Films
Xianhui Zhao,Changhong Li,Qiuping Liu,Yandong Duan,Junjing He,Su Liu,Hai Wang,Song Liang
DOI: https://doi.org/10.1088/1742-6596/419/1/012033
2013-01-01
Journal of Physics Conference Series
Abstract:Colored iron oxide thin films were prepared using Sol-gel technique. The raw materials were tetraethyl orthosilicate (TEOS), etoh ehanol (EtOH), iron nitrate, and de-ionized water. Various properties were measured and analysed, including the colour of thin films, surface topography, UV-Visible spectra, corrosion resistance and hydrophobicity. To understand how these properties influenced the structural and optical properties of Fe2O3 thin films, Scanning Electron Microscope (SEM), UV Spectrophotometer and other facilities were employed. Many parameters influence the performance of thin films, such as film layers, added H2O content, and the amount of polydimethylsiloxane (PDMS). When the volume ratio of TEOS, EtOH and H2O was 15: 13: 1, the quality of Fe(NO3)(3)center dot 9H(2)O was 6g, and pH value was 3, reddish and uniform Fe2O3 thin films with excellent properties were produced. Obtained thin films possessed corrosion resistance in hydrochloric acid with pH=1 and the absorption edge wavelength was similar to 350.2nm. Different H2O contents could result in different morphologies of Fe2O3 nanoparticles. When 1.5 ml PDMS was added into the Sol, thin films possessed hydrophobility without dropping. Coating with different layers, thin films appeared different morphologies. Meanwhile, with the increment of film layers, the absorbance increased gradually.