Abstract:SrO–BaO–B2O3–SiO2 glass-ceramics with a high dielectric constant and low dielectric loss were prepared. The influence of the SiO2/BaO ratio on the sintering behavior, crystallization behavior, and properties were systematically investigated. The results showed that the increasing amount of liquid phase from increasing the SiO2/BaO ratio promoted sintering, resulting in an initial decrease in the sintering activation energy. However, the viscosity of the liquid phase continued to increase, leading to an increase in the sintering temperature and sintering activation energy when the SiO2/BaO ratio reached 0.90. As the SiO2/BaO ratio increased, the fraction of the primary phase BaSi2Al2O8 increased, and its grains grew; the minor phase SrTiO3 was suppressed, resulting in changes in the properties of the glass-ceramics. The sample with a SiO2/BaO ratio of 0.69, which was sintered at 850 °C for 10 min, showed excellent properties: a coefficient of thermal expansion (CTE) of 10.63 × 10−6 K−1 (25–500 °C), a dielectric constant (ϵr) of 16.24 (1 MHz), a dielectric loss (tanδ) of 3.39 × 10−3 (1 MHz), a flexural strength of 138.80 MPa, and a quality loss of acid corrosion of 1.06 × 10−4 g mm−2. The results indicated that the SrO–BaO–B2O3–SiO2 glass-ceramics used in this study have great potential for low-temperature co-fired ceramics applications.

Studies on low-temperature preparation and microwave properties of BaFe12O19 / SiO2-B2O3-K2O microcrystallite glass ceramics

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Low Temperature Sintering and Microwave Dielectric Properties of Ba<sub>4</sub>Nd<sub>9.33</sub>Ti<sub>18</sub>O<sub>54</sub> Ceramics Doped with Crystallizable Glass

Synthesis of a low-firing BaSi2O5 microwave dielectric ceramics with low dielectric constant

Low dielectric and high frequency glass-ceramic in the system CaO-B2O3-SiO2

Low-Temperature Sintering and Microwave Dielectric Properties of Ba5Nb4O15 Ceramics Doped with Glass Sintering Aid

Synthesis and dielectric properties of Ba 2 TiSi 2 O 8 glass-ceramics from the sol–gel process

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

Sintering behaviors and microwave dielectric properties of BaO–MgO–SiO2 ternary ceramics

Synthesis and dielectric properties of Ba<sub>2</sub>TiSi<sub>2</sub>O<sub>8</sub> glass-ceramics from the sol–gel process

Low temperature sintering and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics for LTCC applications

Low-temperature sintering kinetics and dielectric properties of Ba5Nb4O15 with B2O3–SiO2 glass

Microwave Dielectric Properties of Low Temperature Co-Fired Glass–ceramic Based on B2O3–La2O3–MgO Glass with La(Mg0.5Ti0.5)O3 Ceramics

Preparation of B2O3-P2O5-SiO2 glass-ceramics by the sol-gel method

Low-fire Processing of Microwave BaTi4O9 Dielectric with BaO–Li2O–B2O3–SiO2–ZnO Glass

High frequency properties of Ba3CO2-xZnxFe24O41 ceramics sintered at low temperature

Low-Temperature Sintering and Processing of Microwave Dielectric aBaO plus bNb(2)O(5) Ceramics