Effect of slow strain rates on the hydrogen migration and different crack propagation modes in pipeline steel
Zhixian Peng,Chengsi Cao,Feng Huang,Liwang Wang,Zhengliang Xue,Jing Liu
DOI: https://doi.org/10.1002/srin.202300070
IF: 2.1258
2023-03-13
steel research international
Abstract:The slow‐strain‐rate test (SSRT) is the most commonly used method for evaluating pipeline steel in service environments. However, to accurately assess the sensitivity of steel to hydrogen, it is necessary to investigate the effect of different strain rates, taking into account microstructure‐influenced hydrogen migration. In this study, a hot‐rolled X70 pipeline steel sheet was investigated by a slow‐strain‐rate test at different strain rates with and without synchronous hydrogen charging. The influence of the pearlite content and different strain rates on the hydrogen‐assisted crack propagation and hydrogen diffusion in pipeline steels is discussed. Using scanning electron microscopy, electron backscatter diffraction, transmission electron microscopy, and hydrogen microprinting, the hydrogen atoms were observed to be easily segregated at the ferrite/pearlite (F/P) interface without external stress. Under loading, a higher strain rate resulted in lower hydrogen permeation content in steel, penetrating into pearlite and interacting with its internal vacancies, leading to transgranular fracture initiating from pearlite. At a low strain rate, the F/P interface was more vulnerable to hydrogen degradation, leading to intergranular crack mode along the interface and increased tendency to form secondary cracks. Therefore, strain rate‐induced crack initiation and propagation characteristics should be considered during the SSRT. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering