Abstract:Buried pipelines are widely used, so it is necessary to analyze and study their fracture characteristics. The locations of corrosion defects on the pipe are more susceptible to fracture under the influence of internal pressure generated during material transportation. In the open literature, a large number of studies have been conducted on the failure pressure or residual strength of corroded pipelines. On this basis, this study conducts a fracture analysis on buried pipelines with corrosion areas under seismic loads. The extended finite element method was used to model and analyze the buried pipeline under seismic load, and it was found that the stress value at the crack tip was maximum when the circumferential angle of the crack was near 5° in the corrosion area. The changes in the stress field at the crack tip in the corrosion zone of the pipeline under different loads were compared. Based on the BP algorithm, a neural network model that can predict the stress field at the pipe crack tip is established. The neural network is trained using numerical model data, and a prediction model with a prediction error of less than 10% is constructed. The crack tip characteristics were further studied using the BP neural network model, and it was determined that the tip stress fluctuation range is between 450 MPa and 500 MPa. The neural network model is optimized based on the GA algorithm, which solves the problem of convergence difficulties and improves the prediction accuracy. According to the prediction results, it is found that when the internal pressure increases, the corrosion depth will significantly affect the crack tip stress field. The maximum error of the optimized neural network is 5.32%. The calculation data of the optimized neural network model were compared with the calculation data of other models, and it was determined that GA-BPNN has better adaptability in this research problem.

Numerical Study of Crack Propagation in Rich Gas Transporting Pipelines

The Study on Crack Dynamic Propagation in the Rich Gas Transmission Pipelines

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Analysis of Dynamic Fracture Mechanisms in Gas Pipelines

Dynamic fracture study by an experiment/simulation method for rich gas transmission X80 steel pipelines

Evaluation of Blast Wave from Hydrogen Pipeline Burst by a Coupled Fluid-Structure-rupture Approach

ON THE TOUGHNESS-INDUCED CRACK DECELERATION MECHANISM OF GAS PIPELINES TRANSMITTING GAS FROM THE WEST TO THE EAST

Dynamic Ductile Fracture Toughness Test and Numerical Simulation for Ultra-High Pressure Gas Pipelines

Fracture mechanics analysis of gas pipeline with circumferential crack under the action of transverse landslide

The FEM Simulation and Full-Scale Blast Tests for Crack Deceleration in Gas Pipeline

Driving Force and Deformation Analysis for Dynamic Crack Propagation in Gas Pipelines under Different Boundary Conditions

Modeling the Crack Interference in X80 Oil and Gas Pipeline Weld

Fracture process characteristic study during fracture propagation of a CO2 transport network distribution pipeline

THE DEVELOPMENT AND APPLICATION OF THE DYNAMIC FRACTURE ANALYSIS CODE FOR CRACK PROPAGATION INGAS PIPELINES

Crack arrest in rupturing steel gas pipelines

The Toughness-Induced Crack Deceleration Mechanism on Ultra-High Pressure Steel Gas Pipelines

A Damage Mechanics based Evaluation of Dynamic Fracture Resistance in Gas Pipelines

The recent development of analysis methodology for rapid crack propagation and arrest in gas pipelines

Steady State Analysis for Dynamic Crack Propagation in Gas Pipelines

Numerical Simulation and ANN Prediction of Crack Problems within Corrosion Defects

Investigation on crack propagation and reasonable wall thickness of supercritical CO 2 pipeline