Abstract:Magnetic Fe3O4/P (MMA/DVB)((core))-P (St/(GMA/DVB)((shell)) composite microspheres with core-shell structure were prepared by a two-step method. (1) Preparation of the magnetic cores: First, the magnetic miniemulsion composed of organic ferrofluid droplets dispersed in water was obtained by rapid addition of an oil-based magnetite ferrofluid, with a solid content 60 wt%, into the aqueous solution using DNS-86 (polymerizable surfactant) as surfactant in the condition of ultrasonic emulsification. Then, the copolymerization monomers of methyl mathacrylate (MMA) and divinyl benzene (DVB) were injected directly into the magnetic miniemulsion. Because of their hydrophobic character, once the monomers were added into the emulsion, the methyl mathacrylate (MMA) and divinyl benzene (DVB) would have a high tendency to diffuse inside the organic phase of the ferrofluid droplets to form monomer swelling magnetic miniemulsion, Which were supposed to be the main locus for copolymerization. in succession, the temperature was rapidly increased to 70 degrees C and starting the miniemulsion copolymerization to form uniform magnetic latexes. (2) Preparation of the core/shell hybrid polymeric microspheres: Through varying the feeding amount of styrene (St), glycidyl methacrylate (GMA) and DVB, the core-shell structured microspheres were rationally fabricated by the seed emulsion copolymerization using the above magnetic latex as the core emulsion. This preparation process is convenient and effective. Extensive. characterization by X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA) and vibrating sample magnetometer (VSM) showed that the magnetite content of Fe3O4/P(MMA/DVB) composite microspheres was 84 wt %. The magnetite content of the magnetic composite microspheres with core-shell Structure is varied from 20 wt % to 76 wt % by feeding different amount of monomers. The average diameter of the magnetic seeded microspheres and the core-shell composite microspheres is 150 nm and 350 nm, respectively. The functional epoxy groups on the surface of the core-shell composite microspheres can be further modified to load biomolecules.

Preparation of Low Density Magnetic Particle

Novel ferromagnetic nanoparticle composited PACls and their coagulation characteristics.

Preparation and Characterization of Ultra-Fine Cobalt Powder

Influencing Factors on the Uniformity of Electroless Nickel Plating on Cenospheres

Bulk Mg-doped Spherical Lithium Cobalt Oxide Preparation and Characterization of Precursor

Electroless Deposition of Ni-Co-P Deposit on NdFeB Permanent Magnets and Its Corrosion Resistance Property

One-pot synthesis and magnetic properties of hollow Fe<sub>70</sub>Co<sub>30</sub> nanospheres

Properties of bulk magnets prepared by hot pressing using Zn- coated Sm-Fe-N magnetic powder by electrodeposition

Synthesis, Characterization and Magnetic Properties of Hollow Microspheres with Micro-Mesoporous Shells Assembled from Cobalt-Based Ferrocenyl Coordination Polymers

Preparation of Uniform Spherical Magnetite Particles

Porous magnetic carbon spheres with adjustable magnetic-composition and synergistic effect for lightweight microwave absorption

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Electroless Ni-Co-P Coatings on Sintered Nd-Fe-B Magnets with Improved Corrosion Resistance

Synthesis and influence of Zn substitution on optical and magnetic properties of cobalt ferrite nanoparticles by a polyacrylamide gel route

Preparation And Magnetic Properties Of Dense Nicuzn Ferrite By Spark Plasma Sintering

Synthesis of Monodispersed Co(Fe)/Carbon Nanocomposite Microspheres with Very High Saturation Magnetization

Magnetic CoPt Nanoparticles Deposition using Plasma Focus Device

Uniform Magnetic Chains of Hollow Cobalt Mesospheres from One-Pot Synthesis and Their Assembly in Solution

PREPARATION AND CHARACTERIZATION OF MAGNETIC COMPOSITE MICROSPHERES WITH CORE-SHELL STRUCTURE

Mechanical magnetometry of Cobalt nanospheres deposited by focused electron beam at the tip of ultra-soft cantilevers

Characterization and Sedimentation Stability for Dense Suspension System Containing Micron Size