Abstract:Textures and residual stresses are generated during electrodeposition of chromium coatings, which directly affect the performance of the coating. In this work, the variations of texture, hydrogen content, residual stress, microhardness and corrosion resistance of chromium deposited from hexavalent [Cr(VI)] chromium bath using direct current deposited technique were investigated. Electrodeposition experiments were carried out on the low carbon steel substrate by varying the key variable current density. The macrotexture of the coatings was studied by XRD. The crystal orientation and dislocation density were analyzed by EBSD. Residual stress was measured by the indentation method. The research demonstrated that a single preferred orientation on the (222) plane was found at current densities of 20 A/dm 2 , 35 A/dm 2 and 50 A/dm 2 . At 40 A/dm 2 , a mixed preferred orientation on the (222) + (211) planes was discovered. Furthermore, the formation of the chromium coating texture was affected by the variation of hydrogen content, for higher hydrogen promoting grain growth along the (222) crystal plane. Notably, the microstructure-property relationship was developed. At the single preferred orientation of (222) plane, the corrosion resistance was more favorable. At the mixed preferred orientation of (222) + (211) planes, the coating surface achieved higher microhardness, but formed higher residual stress and more microcracks. Moreover, the better electroplating parameter was proposed. At 35 A/dm 2 , the coating had the fewer microcracks and the better overall performance. The higher microhardness of 753 HV was found. The more favorable corrosion resistance was discovered, with the breakdown potential and passive current density of 804.7 mV and 2.220 × 10 −6 A/dm 2 . The lower residual stress of 61 MPa was found, which was about 81 % lower than the maximum stress. It was significant in industry for the enhancement of the service life of substrate and the optimization of the chromium coating process.

Hydrogen-Absorbing and Erosion Resistance of Piston Rods in Automobile Shock Absorber During Fast Chromium Plating

Effect of Current Density and Superfinish on the Corrosion Resistance of Piston Rods in Santana Shock Absorber

Study of the Corrosion Resistance of Automobile Shock Absorber Connecting Rod

Effect Of Processing Parameters On Microstructure And Properties Of Steel-Based Chromium Plating

CHEMICAL PLATING MECHANISM IN ACID BATHS AND FABRICATION OF Ni-P COATING WITH HIGH P CONTENT

Investigations of High-Frequency Induction Hardening Process for Piston Rod of Shock Absorber

Friction Heating Analysis of Piston Rod of Shock Absorber and the Correlation between Temperature and Hardness

Effects of Applied Cathodic Current on Hydrogen Infusion, Embrittlement, and Corrosion-Induced Hydrogen Embrittlement Behaviors of Ultra-High Strength Steel for Automotive Applications

Effect of PVD deposition method on indentation and friction wear characteristics with hydrogen embrittlement of CrN coated stainless steel for electric vehicle hydrogen valves

Effect of current density on the texture, residual stress, microhardness and corrosion resistance of electrodeposited chromium coating

Hard Chromium Plating From A Trivalent Plating Bath

Study of single-metal multi-nanometer electrodeposition chromium layer

The effect of hard chrome plating on iron fines formation

Relationship between Texture, Hydrogen Content, Residual Stress and Corrosion Resistance of Electrodeposited Chromium Coating: Influence of Heat Treatment

Effects of hydrogen permeation on the mechanical characteristics of electroless nickel-plated free-cutting steel for application to the hydrogen valves of hydrogen fuel cell electric vehicles

QPQ treatment of piston rod for high frequency and heavy side load hydraulic cylinders

Experimental and Molecular Dynamics Simulation-Based Investigations on Hydrogen Embrittlement Behavior of Chromium Electroplated 4340 Steel

Zinc-nickel alloy electroplating process

The Effect of Chromium Content on the Corrosion Behavior of Ultrafine-Grained CrXMnFeCoNi High- Entropy Alloys in Sulfuric Acid Solution

Wear Resistance Analysis of Hardening Materials for Engine Cylinder