Abstract:To assess the life of a new diesel aluminium alloy piston under thermal shock loads, thermo-mechanical fatigue (TMF) testing was conducted to characterise the TMF properties of the piston alloy, and an empirical model based on the constraint ratio concept was proposed to predict the TMF life of the piston. Considering that the empirical model required expensive experimental support, a platform with high-frequency induction heating was established to simulate the force on the piston under thermal shock loads to calculate the piston life using the thermal shock test. Additionally, a finite element method was developed to compute the distributions of temperature, strain, and stress during this process. The characteristics of crack initiation and propagation in TMF test rods and piston mock-ups were also investigated. The results showed that the TMF test rod suffered brittle fracture with brittle quasi-cleavage features. The microcracks mainly occurred in primary Si particles due to stress concentration around the primary Si particles induced by the difference between the thermal expansion coefficients of Si and Al. From a macro perspective, the piston initially cracked at the rim above the pinhole, where the stress is larger than that along other directions. From a micro perspective, the protrusions of various sizes on the piston rim were induced by the compression stresses at high temperature. The piston cracks usually initiate around primary Si particles, propagate along the edge of primary Si in a straight line, bifurcate and then stop at a certain depth. If the piston was only heated, cracks or plastic deformations were not produced. The piston life can be assessed using the proposed empirical model based on the constraint ratio concept or thermal shock testing based on the developed platform. The difference between the predicted and experimental life was not greater than 7%.

Investigations of High-Frequency Induction Hardening Process for Piston Rod of Shock Absorber

Investigations of high-frequency induction hardening process for piston rod of shock absorber

Thermal Field FEM Simulation of High-Frequency Induction Hardening for Piston Rod of Shock Absorber

FEM Analysis of High-Frequency Induction Hardening for Piston Rod of Shock Absorber

Development of Powder Metallurgy High Speed Steel

Friction Heating Analysis of Piston Rod of Shock Absorber and the Correlation between Temperature and Hardness

Calculation and Analysis of Piston Thermal Shock by Using Plate Model

Hydrogen-Absorbing and Erosion Resistance of Piston Rods in Automobile Shock Absorber During Fast Chromium Plating

Effect of Current Density and Superfinish on the Corrosion Resistance of Piston Rods in Santana Shock Absorber

QPQ treatment of piston rod for high frequency and heavy side load hydraulic cylinders

Study on Mechanism of Laser Thermal Damage on Piston

Experimental Investigation on the Sharpness Reduction of an Axial Piston Pump with Reinforced Shell

Relief of Strain Hardening in Deformed Inconel 718 by High-Density Pulsed Electric Current

The Effect of Surface Hardening on The HQ 705 Steel Camshaft Using Static Induction Hardening and Tempering Method

Failure Analysis and Measures of Piston Rod of Reciprocating Compressor

Influence of Piston Mass and Working Pressure on the Impact Performance of a Hydraulic Rock Drill Using the Stress Wave Method

Study of the Corrosion Resistance of Automobile Shock Absorber Connecting Rod

RE-nitrocarburizing Technology for Piston Rod Made of 40Crmnmo

Experimental and Computational Study on Thermo‐mechanical Fatigue Life of Aluminium Alloy Piston

Failure analysis of the piston used in a pneumatic down the hole impactor

Optimization of Induction Hardening for Sprocket Based on Numerical Simulation and Experiment Design