Abstract:The effect of the Al2O3-SiO2 short fiber on the solidification processing of the alpha-Al and Al-Si eutectic phases in the LD11 alloys was studied by the optical microscope (OM), differential scanning calorimeter (DSC) and scanning electron microscopy (SEM). The results revealed that the a-Al phase nucleated in the inter-fiber spacing then grew towards the fiber. However, the eutectic silicon nucleated on the fiber surface and grew towards the inter-fiber spacing. It was further proved by the DSC measurement that growth processing of the a-Al phase was restricted by the fiber, but nucleation behavior of the alpha-Al phase was not affected by the fiber. In contrast to the (alpha-Al, the nucleation and growth processing of the eutectic silicon was accelerated by the fiber.

Study Of The Nucleation And Growth Behavior Of Al2o3-Sio2/Ld11 Composites Fabricated By Squeeze Casting Method