Synthesis and Reaction Path of Ti‐Al‐C MAX Phase by Reaction with Ti‐Al Intermetallic Compounds and TiC
Hojun Lee,Si Yeon Kim,Young‐In Lee,Jongmin Byun
DOI: https://doi.org/10.1111/jace.19217
IF: 4.186
2023-06-02
Journal of the American Ceramic Society
Abstract:In this study, it was verified that the synthesis of a Ti‐Al‐C MAX phase has advantages when using intermetallic compounds rather than using only elemental powders. The formation behavior of the MAX phase was presented through diffusion experiments. In the case of using elemental powder, Ti2AlC is produced at 1,300°C, and Ti3AlC2 is produced at 1,400°C. When intermetallic compounds are used, Ti2AlC is produced at 1,000°C, and Ti3AlC2 is produced at 1,300°C. In the case of the elemental powder, it is verified that Ti3AlC2 content is decreased and Ti2AlC is increased when heat treatment is performed at 1,400°C for 3 h. Rather Ti3AlC2 content is increased when intermetallic compounds are used. When an intermetallic compound is used, synthesis occurs more actively at high temperatures, and the tendency to be thermally decomposed can be prevented. When TiAl and TiC are heat treated, Al of the intermetallic compound is diffused into TiC, and C of TiC is diffused into the intermetallic compound. Furthermore, there are many two‐dimensional defects in TiAl, which act as a C diffusion channel. C diffuses into TiAl to produce TiCX, and the MAX phase is generated by the short‐range diffusion of Al. In the case of TiC, TiC transform into TiCX after C diffuses into TiAl, which consequently structure of TiC changes from Cubic to Hexagonal. This is the same crystal structure as the MAX phase, and it is confirmed that the (110) surface is maintained. A Ti‐C layer structure of the (110) surface is maintained, and it was determined that Al is diffused during this time to generate MAX phase. This article is protected by copyright. All rights reserved
materials science, ceramics