Magnetoresistance effect observed in Fe/Mo multi-layers prepared by electron beam evaporation

tongchuan he,Bin Zhao,yanqin gao,Fei Zeng,Feng Pan

2003-01-01

Acta Metallurgica Sinica (English Letters)

Abstract:The Fe/Mo multilayers were prepared by electron beam evaporation, the. micro structure and magnetic properties of the multilayers were studied by X-ray diffraction, vibrating-sample magnetometer (VSM) et al. The experimental results revealed that the Fe/Mo multilayers in our experimental conditions behaved magnetoresistance effect with a sharp peak on magnetoresistance (MR) ratio curve, and magnetoresistance is easily saturated at low applied magnetic fields. For [Fe(1.5 nm)/Mo(1.0 nm)]42 multilayers, MR ratio could arrive to 0.1%. The antiferromagnetic interlayer coupling could be observed in some films at room temperature. The strength of the antiferromagnetic interlayer coupling J in the films is low because of the low saturation field Hs. The relationship between magnetic properties and microstructure was also discussed.