Texture and Magnetic Domain of Nanocomposite NdFeB Permanent Magnetic Alloys

陈烨,姜忠良,陈秀云,白飞明,章莱,朱静

DOI: https://doi.org/10.3321/j.issn:1000-0054.2003.10.002

2003-01-01

Abstract:A high performance nanocomposite magnetic material was developed using the melt spinning method to fabricate anisotropic nanocomposite ribbons. Xray diffraction showed that the ribbons for Nd9Fe85-xNbxB6(x=0,0.5,1.0) were textured with Nd2Fe14B perpendicular to the surface of the ribbons. The texture was more pronounced on the free surface than on the contact surface. Addition of up to x=1.0 Nb increased the degree of preferred orientation (DPO) and a DPO of 94% was obtained with a spinning velocity of 15 m·s-1. Magnetic force microscope observations show that strong exchange coupling exists between the grains. A sample with x=0.5 has both strong exchange coupling and a high degree of texture, which results in the best magnetic properties of a remanent magnetic polarization density of 1.130 T, an intrinsic coercivity of 519.8 kA·m-1 and a maximum energy product of 121.2 kJ·m-3. 