Microstructure and mechanical properties of SiCnp/Al6082 aluminum matrix composites prepared by squeeze casting combined with stir casting
Junwen Zhu,Wenming Jiang,Guangyu Li,Feng Guan,Yang Yu,Zitian Fan
DOI: https://doi.org/10.1016/j.jmatprotec.2020.116699
IF: 6.3
2020-09-01
Journal of Materials Processing Technology
Abstract:<p>In this work, SiC<sub>np</sub>/Al6082 aluminum matrix composites were prepared by squeeze casting (SC) combined with stir casting, and the effects of nano-sized SiC particles (SiC<sub>np</sub>) and SC on microstructure and mechanical properties of the 6082 aluminum alloy were investigated. The result shows that the SiC<sub>np</sub> were uniformly distributed in the 6082 aluminum matrix alloy using the stir casting. With the addition of the SiC<sub>np</sub>, the microstructure of the 6082 aluminum alloy was obviously refined, up to 30.55% grain refinement compared to the 6082 aluminum alloy without the addition of the SiC<sub>np</sub>. The as-cast ultimate tensile strength, yield strength and elongation of the SiC<sub>np</sub>/Al6082 aluminum matrix composites were enhanced, which increased by 8.92%, 12.16%, and 12.60%, respectively, compared with the 6082 matrix alloy without the SiC<sub>np</sub>. After the SC, the compactness of the SiC<sub>np</sub>/Al6082 composites was significantly improved, and the grain of the composites was further refined. The ultimate tensile strength, yield strength and elongation of the SiC<sub>np</sub>/Al6082 composites fabricated by the SC respectively increased by 29.81%, 43.18%, and 226.28%, compared to the 6082 aluminum alloy obtained by gravity casting (GC).</p>
materials science, multidisciplinary,engineering, manufacturing, industrial