Microstructure and mechanical properties of SiCnp/Al6082 aluminum matrix composites prepared by squeeze casting combined with stir casting

Junwen Zhu,Wenming Jiang,Guangyu Li,Feng Guan,Yang Yu,Zitian Fan
DOI: https://doi.org/10.1016/j.jmatprotec.2020.116699
IF: 6.3
2020-09-01
Journal of Materials Processing Technology
Abstract:<p>In this work, SiC<sub>np</sub>/Al6082 aluminum matrix composites were prepared by squeeze casting (SC) combined with stir casting, and the effects of nano-sized SiC particles (SiC<sub>np</sub>) and SC on microstructure and mechanical properties of the 6082 aluminum alloy were investigated. The result shows that the SiC<sub>np</sub> were uniformly distributed in the 6082 aluminum matrix alloy using the stir casting. With the addition of the SiC<sub>np</sub>, the microstructure of the 6082 aluminum alloy was obviously refined, up to 30.55% grain refinement compared to the 6082 aluminum alloy without the addition of the SiC<sub>np</sub>. The as-cast ultimate tensile strength, yield strength and elongation of the SiC<sub>np</sub>/Al6082 aluminum matrix composites were enhanced, which increased by 8.92%, 12.16%, and 12.60%, respectively, compared with the 6082 matrix alloy without the SiC<sub>np</sub>. After the SC, the compactness of the SiC<sub>np</sub>/Al6082 composites was significantly improved, and the grain of the composites was further refined. The ultimate tensile strength, yield strength and elongation of the SiC<sub>np</sub>/Al6082 composites fabricated by the SC respectively increased by 29.81%, 43.18%, and 226.28%, compared to the 6082 aluminum alloy obtained by gravity casting (GC).</p>
materials science, multidisciplinary,engineering, manufacturing, industrial
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to prepare Al6082 aluminum - based composites reinforced by SiC nanoparticles through squeeze casting combined with stir - casting methods, and to study the effects of nano - sized SiC particles (SiC np) and squeeze casting on the microstructure and mechanical properties of Al6082 aluminum alloy. Specifically, the paper focuses on the following aspects: 1. **Dispersion of nano - sized SiC particles**: Study the dispersion of nano - sized SiC particles in the Al6082 aluminum alloy matrix and the influence of this dispersion on the microstructure of the material. 2. **Refinement of microstructure**: Explore the effects of nano - sized SiC particles and squeeze casting on the grain refinement of Al6082 aluminum alloy, and the improvement of material properties due to this refinement. 3. **Improvement of mechanical properties**: Evaluate the effects of nano - sized SiC particles and squeeze casting on the tensile strength, yield strength and elongation of Al6082 aluminum alloy, especially whether these performance indicators are improved after adding nano - sized SiC particles. 4. **Effect of heat treatment**: Study the further effects of heat treatment on the microstructure and mechanical properties of SiC np/Al6082 composites, especially the effect on improving the comprehensive properties of the material. The paper verifies the effectiveness and feasibility of nano - sized SiC particles and squeeze - casting methods in improving the properties of Al6082 aluminum alloy through experiments, providing theoretical basis and technical support for the development of high - performance aluminum alloy composites.