SYNTHESIS OF TiB2-TiC COMPOSITE POWDER BY SHS REDUCTION PROCESS

王业亮,傅正义,王皓,张金咏

DOI: https://doi.org/10.3321/j.issn:1000-3851.2003.01.004

2003-01-01

Abstract:The mechanism of chemical reaction and microstructure formation process of B2O3TiO2MgC system were investigated in this paper. The results showed that TiB2TiC ceramic powder could be obtained by SHS from B2O3TiO2MgC system. The results of analysis of different thermal analysis (DTA) and Xray diffraction (XRD) showed the following thermal processes of B2O3TiO2MgC system: B2O3 was reduced to B and TiO2 was reduced to Ti. Metal Mg was melted at 650 ℃. At 680 ℃ the reaction between B and Ti nearly finished and the formation of TiC from the reaction of Ti and C began. TiO2 was reduced to element Ti step by step through the following way: TiO2→TiO→Ti. TiB2TiC composite powder with particle size of 45 percent under 1 μm and 87 percent under 3 μm was obtained after MgO, the unwanted phase, was removed by leaching in hydrochloric acid. Results of SEM micrographs of TiB2TiC ceramic multiphase powder showed that the particle size is much smaller than that of single phase TiB2 or TiC produced by the same methods. The mole ratio of Ti and C in TiC was 1∶0.7483.