Abstract:Different nanocrystalline magnesium with carbon layers were successfully synthesized via a facile wet-chemical ball milling method for 20, 30 and 40 h, respectively. Based on Scherrer formula and X-ray diffraction results, the average crystallite size of all the three samples was below 30 nm. TEM observations showed that the hydrogenated Mg particles were covered with carbon layers. Moreover, the 40 h ball milled Mg sample showed outstanding hydrogen storage performance especially in the aspect of hydrogen absorption. The as-prepared sample started to take up hydrogen at nearly room temperature and eventually absorbed 6.8 wt% hydrogen at 200 degrees C. The apparent activation energy (E-a) of hydrogen absorption for the sample was decreased to 26.7 kJ/mol, much lower than that of other reported systems. For the dehydrogenation experiments, the hydrogenated sample could start to release hydrogen at about 275 degrees C and 6.5 wt% hydrogen was desorbed in 20 min at 325 degrees C. Interestingly, the prepared samples showed noteworthy air stability. Been placed in the air for 60 min, the dehydrogenation kinetics and hydrogen capacity of the three samples were basically unchanged, making it possible to be used in future commercial applications. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Hydrogen Storage Properties of MgNiCu-CrCl3 and Ignition in Hydriding Process

Hydrogen storage properties of nanocomposite Mg–Ni–Cu–CrCl3 prepared by mechanical alloying

Hydrogen Storage Properties of the Mg–Ni–CrCl3 Nanocomposite

Properties of Hydriding and Dehydriding of Nanocrystalline Composite of Mg-Ni-Cr2O3

Sorption Properties of Mg-Ni-Crcl3 Hydrogen Storage Composite

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Hydrogen Storage Properties of Nanocomposite Mg-Ni-MnO2 Made by Mechanical Milling

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

Hydrogen storage properties of nanocomposite Mg-Ni-V2O5

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Hydriding Characteristics of Mg2NiMg2Ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Structure and Hydrogenation Properties of Nanocrystalline Mg2Ni Prepared by Hydriding Combustion Synthesis and Mechanical Milling

Hydriding Characteristics of Mg2ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

Hydrogen Storage Properties of Nanocrystalline Mg2Ni Prepared from Compressed 2mgh2ni Powder

Hydrogen Storage Properties of Mg-based Materials with CNTs

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Hydrogen storage properties of Mg-23.3wt.%Ni eutectic alloy prepared via hydriding combustion synthesis followed by mechanical milling

Construction of Carbon Covered Mg2NiH4 Nanocrystalline for Hydrogen Storage

Hydrogen Storage Properties of Mg100−xNix (x = 5, 11.3, 20, 25) Composites Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling (HCS + MM)