Abstract:Reducing Mg particles to nanoscale and doping with various catalysts are considered as efficient approaches for improving the hydrogen storage properties of Mg/MgH2. It has been established that doping Ni or Mg2Ni into nano-Mg/MgH2 through physical routes remarkably improves the hydrogen sorption kinetics. In this work, a Mg-Ni nanocomposite has been coprecipitated from a tetrahydrofuran (THF) solution containing anhydrous magnesium chloride (MgCl2), nickel chloride (NiCl2), and lithium naphthalide (LiNp) as the reducing agent. TEM observations reveal that Ni nanoparticles are distributed homogeneously on the surface of those larger Mg particles with sizes ranging from 10 to 20 nm in the nanocomposite. It is observed that gamma-MgH2 phase appears when the nanocomposite is hydrogenated at temperatures below 225 degrees C. Pressure-composition-temperature (PCT) measurements reveal that the Mg-Ni nanocomposite has superior hydrogen storage properties over the pure Mg prepared using the same method. For instance, the Mg-Ni nanocomposite can absorb 85% of its maximum hydrogen capacity within 45 s at 125 degrees C, and a hydrogen capacity of 5.6 wt % can be obtained within 10 h at room temperature. In addition, the dehydrogenation temperature of the hydrogenated Mg-Ni nanocomposite is also much lower than that of the hydrogenated pure Mg. The hydrogenation and dehydrogenation enthalpies of the Mg-Ni nanocomposite are determined to be -70.0 and 70.7 kJ/mol H-2, slightly lower than those for the reduced pure Mg. The excellent hydrogen sorption properties of the Mg-Ni nanocomposite can be attributed to the nanosize effect of Mg particles and the gateway effect of Mg2Ni formed in the composite after hydrogenation/dehydrogenation cycles.

Hydrogen Storage Properties of Nanocomposite Mg-Ni-MnO2 Made by Mechanical Milling

Hydrogen storage properties of nanocomposite Mg-Ni-V2O5

Research on hydrogen storage properties of Mg–3Ni–2MnO2(wt.%) milled with nickel powders of different particle sizes

Cyclic Hydrogen Storage Properties of Mg Milled with Nickel Nano-Powders and Mno2

Hydrogen storage properties of nanocomposite Mg–Ni–Cu–CrCl3 prepared by mechanical alloying

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Hydrolysis of hydrided Mg-3Ni-2MnO2 Composites prepared by ball milling for hydrogen production

Hydrogen Storage Properties of Mg-based Materials with CNTs

Hydrogen Storage Properties of Mg100−xNix (x = 5, 11.3, 20, 25) Composites Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling (HCS + MM)

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

Hydrogen Storage Properties of Nanocrystalline Mg2Ni Prepared from Compressed 2mgh2ni Powder

Remarkably Improved Hydrogen Storage Properties of Carbon Layers Covered Nanocrystalline Mg with Certain Air Stability

Hydrogen Storage Properties of a Mg–Ni Nanocomposite Coprecipitated from Solution

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Hydriding Characteristics of Mg2NiMg2Ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Hydriding Characteristics of Mg2ni Prepared by Mechanical Milling of the Product of Hydriding Combustion Synthesis

Hydrogenation Properties of Mechanically Milled Mg2Ni0.8Cr0.2-CoO/Al2O3 Composites.

Properties of Hydriding and Dehydriding of Nanocrystalline Composite of Mg-Ni-Cr2O3

Sorption Properties of Mg-Ni-Crcl3 Hydrogen Storage Composite