Mössbauer Study of Fe-Co Nanowires

ZY Chen,QF Zhan,DS Xue,FS Li,XZ Zhou,H Kunkel,G Williams
DOI: https://doi.org/10.1088/0953-8984/14/3/328
2002-01-01
Journal of Physics Condensed Matter
Abstract:Arrays of Fe1-xCox (0.0 less than or equal to x less than or equal to 0.92) nanowires have been prepared by an electrochemical process, co-depositing Fe and Co atoms into the pores of anodic aluminium; their compositions were determined by atomic absorption spectroscopy. Transmission electron microscope results show that the nanowires are regularly spaced and uniform in shape with lengths of about 7.5 mum and diameters of 20 nm. The x-ray diffraction indicates a texture in the deposited nanowires. For the composition below 82 at.% cobalt, the nanowires had a body-centred-cubic structure with a [110] preferred orientation. For the 92 at.% cobalt sample, the alloy exhibited a mixture of bcc and face-centred-cubic structure. The room temperature Fe-57 Mossbauer spectra of the arrays of Fe1-xCox nanowires have second and fifth absorption lines of the six-line pattern with almost zero intensity, indicating that the internal magnetic field in the nanowires lies along the long axis of the nanowire. The maximum values of the hyperfine field (B-hf = 36.6 +/- 0.1 T) and isomer shift (IS = 0.06 +/- 0.01 mm s(-1)) occur for 44 at.% cobalt. The variations of the isomer shift and the linewidths with composition indicate that the Fe1-xCox alloy nanowires around the equiatomic composition are in an atomistic disordered state.
What problem does this paper attempt to address?