Solidification Characteristics of Molten Pool and Formation Mechanism of Microstructure of Light Beam Surfacing Layer

JG Shan,H Li,JL Ren

DOI: https://doi.org/10.3321/j.issn:0412-1961.2002.05.022

IF: 1.797

2002-01-01

ACTA METALLURGICA SINICA

Abstract:The solidification characteristics of the molten pool and the formation mechanism of the microstructure during light beam surfacing process with pre -placed powder as well as powder feeding were investigated by using OM, SEM, EDS and XRD. Results indicate that the light beam surfacing layer with high energy input is consisted of epitaxially growing r(Fe, Ni) planar crystal in the bottom of the layer and r(Fe, Ni) dendrite which was growing opposite the heat flux with preferred orientation. The angle between the dendrite and the direction of light beam scanning in the top of the layer is smaller than that in the bottom of the layer. The matrix in the surfacing layer is r(Fe, Ni) phase and more Cr was contained in later formed r(Fe, Ni) phase. During the surfacing process, Cr23C6 was precipitated in the layer with the pre-placed powder, which was caused by Cr and C accumulation in local region, but Cr5B3 was precipitated in local region in the powder feeding surfacing layer, which was caused by lower loss of B and Si by less overheating.