Abstract:Hot cracking in laser powder bed fused (LPBF) Al x CoCrFeNi high entropy alloys (HEAs) plague the production of high strength parts. Here we show that the body-centered cubic (BCC) phase with very high hardness (~670 HV) in LPBF printed Al x CoCrFeNi(x=1, 0.7) HEAs causes cracking due to the plastic incompatibility between grain boundaries. To mitigate this, we propose a BCC to face-centered cubic (FCC) transformation strategy in the Al x CoCrFeNi HEAs to inhibit cracking and found that the Al 0.5 CoCrFeNi alloy (i.e., when x = 0.5) with a single FCC crystal structure possess low cracking sensitivity and well intergranular plastic compatibility, accompanied with decreased residual stress confirmed by using X-ray diffraction testing. The mechanical properties of the LPBF printed Al 0.5 CoCrFeNi HEA can be further enhanced by precipitation heat treatment. Scanning electron microscope/ transmission electron microscopy analysis show that nano-sized B2, L12 and σ phases precipitated from FCC Al 0.5 CoCrFeNi HEA when aged at 700°C for 1 h. The ultimate tensile strength (UTS) increases from 899 MPa (as-print) to 1552 MPa (aged) with the elongation decreasing from 35.6% (as-print) to 7.1% (aged) due to the Orowan bypass mechanism of nano-precipitates. An increased aging temperature to 800-1000°C, decreases the UTS while increases the elongation, accompanied by the L12-to-B2 transformation and B2 phase coarsening. The deformation mechanism is mainly dominated by dislocations and stacking faults in the Al 0.5 CoCrFeNi HEA sample.

Phase Evolution and Solidification Cracking Sensibility in Laser Remelting Treatment of the Plasma-Sprayed CrMnFeCoNi High Entropy Alloy Coating

Research on hot cracking in laser welding of Al-contaminated CoCrFeMnNi high-entropy alloys

Cracking Mechanism and Mechanical Properties of Selective Laser Melted CoCrFeMnNi High Entropy Alloy Using Different Scanning Strategies

Crack Formation and Control in an AlCoCrFeNi High Entropy Alloy Fabricated by Selective Laser Melting

Formation and beneficial effects of the amorphous/nanocrystalline phase in laser remelted (FeCoCrNi)75Nb10B8Si7 high-entropy alloy coatings fabricated by plasma cladding

Anisotropic Response of CoCrFeMnNi High-Entropy Alloy Fabricated by Selective Laser Melting

Glass phase microstructure and mechanical behaviors of laser-remelted Ni30Cr25Al15Co15Mo5Ti5Y5 coating reinforced by α/γ-Al2O3 phase

Microstructure and character of laser remelting of plasma sprayed coating (Ni-Cr-B-Si) on Al-Si alloy

Hot cracking behavior and mechanism of the IC10 directionally solidified superalloy during laser re-melting

Cyclic plasticity and fatigue damage of CrMnFeCoNi high entropy alloy fabricated by laser powder-bed fusion

Selective laser melting of AlCoCrFeMnNi high entropy alloy: Effect of heat treatment

Cracking Behavior of Laser Cladding Forming Nickel Based Alloys

Cracking Mechanism and Susceptibility of Laser Melting Deposited Inconel 738 Superalloy

The Effect of Thermal Cycle on Hot Cracking Evolution and Formation Mechanism in Thin Wall, Single Layer, and Cubic Samples of High-Strength Al-Cu-Mg-Mn Alloys Fabricated by Laser Powder Bed Fusion

Liquefaction Characteristics and Cracking Behavior of the Grain Boundaries and Interdendritic Regions in Non-Weldable K447A Superalloy During Laser Re-Melting

Cracks Suppression Strategies for CoCrNi Medium Entropy Alloy Fabricated by Laser Directed Energy Deposition

Microstructure characterization of AlCoCrFeNiTi high-entropy alloy coating produced by atmospheric plasma spraying

Inhibiting cracking and improving strength for additive manufactured Al x CoCrFeNi high entropy alloy via changing crystal structure from BCC-to-FCC

Effect of laser remelting on microstructure, salt spray corrosion and electrochemical performance of plasma sprayed CoCrFeNiMo HEA coating

Research on the Mechanical Properties of AlCoCrFeNi + CoCrNi Fabricated by Laser Melting Deposition

Liquation Cracking Facilitated by Stray-Grain Chains in a High-Γ’-content Nickel-Based Alloy K4002 Produced Via Electron Beam Powder Bed Fusion