Abstract:In this study, the recycled Al-Mg-Mn-Fe alloys having different Fe levels (0.1%, 0.5%, and 0.8%) were successfully developed by applying squeeze casting without heat treatment. Optical and scanning electron microscopy, synchrotron X-ray tomography and radiography, X-ray diffraction, and tensile tests combined with thermodynamic calculations were used to study the correlation between the microstructural evolution and mechanical properties. The results showed that for the alloys with an applied pressure of 75 MPa, as the Fe increase from 0.1% to 0.8%, the yield strength (YS), and ultimate tensile strength (UTS) increased from 122 MPa and 244–146 MPa and 289 MPa, and elongation decreased from 34% to 12%. Even though Fe additions increased the volume fraction of Fe-rich intermetallic phases, it significantly increased the UTS and YS. The synchrotron X-ray tomography and deep-etched results both show that the 3D morphology changed from individual Chinese-script to interconnected plate-like. The 3D morphology of 0.8Fe alloy clearly demonstrate that the hole partially or whole penetrated the entire rectangle-shaped Al6(FeMn) phases, which is due to the close-packed plane growth. In-situ synchrotron X-ray radiography results showed the facet growth behaviour of Al6(FeMn) in 0.8Fe alloys during solidification with a long needle-like shape. The size of primary Al6(FeMn) phases decreases, whereas their number increases with increasing cooling rate. Moreover, the applied pressure was beneficial in refining the size of α-Al grains and Fe-rich phases and reducing the volume fraction of pores, thus contributing to the improvement of strength and elongation. The in-situ tensile test results indicated that the crack initiated in the Fe-rich phases and pores, and the slip lines were blocked by the Fe-rich phases resulting in the strengthening of the secondary phases.

Effect of Fe on the formation of NiAl intermetallic light beam surfacing layer and its microstructure

Formation and Precipitation Phases of Ni-Al System Intermetallic Surfacing Layers by Light Beam Heating

Effect of heat input on precipitation characteristic and order degree of Ni3Al in light beam surfacing layer

Effect of Fe Addition on Microstructure and Properties of Al-3ni Alloys

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

MICROSTRUCTURE AND STRENGTHENING MECHANISM OF Ni-BASED ALLOY POWDER SURFACING LAYER BY LIGHT BEAM

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Solidification Characteristics of Molten Pool and Formation Mechanism of Microstructure of Light Beam Surfacing Layer

Characterisation of Fe Distribution in the Liquid–Solid Boundary of Al–Zn–Mg–Si Alloy Using Synchrotron X-ray Fluorescence Microscopy

Effect of Ni addition on the microstructure, conductivities and mechanical properties of as-cast Al-Fe alloys

Dilution Rate and Microstructure of TIG Arc Ni-Al Powder Surfacing Layer

Enhanced bonding strength of Al/Fe bimetal by Ni-based alloys Ni-based interlayer prepared by laser cladding technique

Study on the microstructure and properties of a laser cladding Fe–Ni–Al coating based on the invar effect

The composite microstructures’ effect on the mechanical properties of Ni–25Al–xFe intermetallics

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Improvement of Microstructure and Sliding Wear Property of Cold-Sprayed FeAl Intermetallic Compound Coating by Annealing Treatment

Effect of Fe and Mn additions on microstructure and wear properties of spray-deposited Al–20Si alloy

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Effect of high entropy alloy as the interlayer on the interfacial microstructure and mechanical property of Al/steel bimetal by compound casting

Interfacial characteristics and wear properties of laser fabricated Fe‒Al coatings on 6061 aluminum alloy

Effect of Initial Fe Content on Microstructure and Mechanical Properties of Recycled Al-7.0Si-Fe-Mn Alloys with Constant Mn/Fe Ratio