Abstract:In this study, A356 matrix and 0.2 vol%∼0.8 vol% in-situ Al2O3p/A356 composite were hot rolled to 75% reduction ratio and 0.6 vol% composite was hot rolled to 75% and 83% reduction ratios. Scanning electron microscope (SEM), Electron back scattering diffraction (EBSD) and transmission electron microscopy (TEM) were used to characterize the microstructure and texture evolution so as to investigate the effect of the particle content and reduction ratios. In the 75% rolling reduction, the Si phase in the A356 matrix and Al2O3p/A356 composites was fragmented and distributed along the rolling direction (RD), obvious Al2O3 agglomeration diminished. On the state of 75% reduction, when the content of Al2O3 was 0.2 vol%, the composite had the finest grain size, however the 0.6 vol% composite had a better Si phase and Al2O3 distribution. The Al2O3 particle in 0.2 vol% sample can enhance the dislocation density and accelerate the sub-grain boundary formation. For the 75% reduction materials, the tensile properties increased with increase of particulate content to 0.6 vol% then decreased. The mechanical properties of 83% rolling reduction sample was better than the 75% reduction. Tensile tests showed that the ultimate tensile strength (UTS), yield strength (YS) and elongation (El) of 0.6 vol% Al2O3p/A356 composite increased to 282 MPa, 221 MPa and 17.5%, respectively, due to the uniform distribution of the particles and refined Si phase upon increasing the rolling reduction to 83%, in combination with T4 heat treatment. In addition, the mechanisms of particle dispersion, recrystallization grain refinement and strengthening are also discussed.

Study on Interface Between Sub-Micron Particles and Matrix in Al2o3p/Al Composites

High-Resolution Electron Microscope Observation of Interface Microstructure of A Cast Al-Mg-Si-Bi-Pb(6262)/Al2o3p Composite

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

In situ fabrication and microstructure of Al2O3 particles reinforced aluminum matrix composites

Interfacial Segregation and Precipitates Behavior in the Ultrafine Grained Al-based Metal Matrix Composites

Influence of particulate B4C with high weight fraction on microstructure and mechanical behavior of an Al-based metal matrix composite

Study on microstructure of Al2O3/SiC nanocomposites

Modify the interface between ex-situ γ-Al2O3 and Al matrix via in-situ coating in an Al matrix composite

Effect of surface modification of Al2O3 powder with Y2O3 on microstructure and tensile properties of aluninium matrix composites

Microstructure and interface analysis of rare-earth modified-Al2O3 particle/6061A1 composites

Microstructure study of hot rolling nanosized in-situ Al2O3 particle reinforced A356 matrix composites

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Interface Investigations of Alumina and Aluminosilicate Short-Fiber-reinforced Aluminum-Alloy Composites

Microstructure and Mechanical Properties of Al/Al4C3/Al2O3 Composite

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Effect of Surface Modification of Sub-Micron Al2O3 Particles by Rare-Earth on Interfacial Wettability of Al Matrix Composites

Rare-Earth Oxide Coating for Sub-Micro Particulates Reinforced Aluminum Matrix Composites

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Y2O3 MODIFIED-Al2O3 PARTICLE /6061Al COMPOSITES

High strength Al<SUB>2</SUB>O<SUB>3p</SUB>/6061 Al composites: effect of particles, subgrains and precipitates

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents