Abstract:In this paper, dense MAX phase Ti3AlC2 enhanced and toughened TiAl3 matrix composites with mass fractions of 10∼40% were prepared by in-situ reaction via powder metallurgy route which using TiH2, Al and TiC powder as the starting materials. Then, the microstructure and phase structure of the composites were characterized, and the relationship between microstructure, mechanical properties and fracture mechanism was systematically investigated. The results show that the lath-like (micron level) and fine-needle-like (submicron level) reinforcements Ti3AlC2 are uniformly distributed in TiAl3 matrix. With the increases of mass fraction of reinforcements, the average grain size of the TiAl3 matrix decreases remarkably from 7.6 μm to 4.8 μm, indicating that the reinforcements Ti3AlC2 can effectively refine the matrix grains and plays a good pinning effect on the TiAl3 matrix. The prepared Ti3AlC2/TiAl3 composite with 30% mass fraction exhibits excellent comprehensive mechanical properties: the Vickers hardness, flexural strength, fracture toughness is 575 ± 5 HV, 470 ± 18 MPa, and 3.83 ± 0.05 MPa m1/2, 14.1%, 174.9% and 117.6% higher than that of the pure TiAl3 matrix, respectively. Both the strengthening and toughening effects are significant. The strengthening mechanism are fine grain strengthening and deformation strengthening, while the toughening mechanism is a synthetic effect in terms of crack deflection, crack bifurcation, grain refinement and stress-induced microcrack. Fracture analysis shows that the fracture mechanism is transgranular (cleavage) fracture.

Modify the interface between ex-situ γ-Al2O3 and Al matrix via in-situ coating in an Al matrix composite

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

High-Resolution Electron Microscope Observation of Interface Microstructure of A Cast Al-Mg-Si-Bi-Pb(6262)/Al2o3p Composite

In situ fabrication and microstructure of Al2O3 particles reinforced aluminum matrix composites

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

In–situ synthesis of an Al composite reinforced with multi–scale Al12Mo, (Al, Zr, Si) and Al2O3 particles through a multi–stage reaction

Synthesis and characterization of an in-situ Al2O3/Al–Cu composite with a heterogeneous structure

Effectively enhanced strength by interfacial reactions in in-situ carbon reinforced Al matrix composites

Effect of surface modification of Al2O3 powder with Y2O3 on microstructure and tensile properties of aluninium matrix composites

Achieving high combination of strength and ductility of Al matrix composite via in-situ formed Ti-Al3Ti core-shell particle

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Effect of MgO particles with in-situ graphene coating on mechanical and thermal expansion properties of aluminum matrix composites

Rare-Earth Oxide Coating for Sub-Micro Particulates Reinforced Aluminum Matrix Composites

In situ Al2O3 particle-reinforced Al and Cu matrix composites synthesized by displacement reactions

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

In-situ synthesis of Al2O3-reinforced high Nb–TiAl laminated composite with an enhanced strength-toughness performance

Enhanced Combination of Strength and Ductility in Ultrafine-Grained Aluminum Composites Reinforced with High Content Intragranular Nanoparticles