Abstract:In fatigue experiments of NiTi shape-memory alloys (SMAs), TiC inclusions have been found to cause cracks. Based on bending-rotation fatigue (BRF) experiments, which have evolved as one standard method to study the structural fatigue of superelastic NiTi wires, the influence of TiC inclusions on the fatigue behavior of NiTi SMAs has been analyzed quantitatively in this article. Aurichio’s superelastic model was implemented into the finite element (FE) code ABAQUS. One specimen without inclusion and seven specimens with inclusions, at different distances with respect to the neutral axis of the wire specimens, have been analyzed. The stress distributions at the cross sections are nonlinear, and there is a stress plateau in the cross section when the phase transformation occurs. The stress distribution in the cross section of the specimen without inclusion is not only dependent on the load, but also dependent on the loading path and loading history. On the other hand, the maximum stress of the specimen without inclusion is not always at the surface, which is due to the phase transformation behavior of SMAs. The existence of the inclusions changes the stress distributions in the cross section. The maximum stress is dependent on the position of the inclusions, the load, and the loading path. It has been found that the maximum stresses increase as the distance from the inclusion to the neutral axis increases. When the inclusion is at the specimen surface, the maximum stress is the highest among all the studied cases. Such high stresses caused by the inclusions can easily induce fatigue cracks. The simulation can explain the fatigue behavior of BRF experiments and provide a deep insight into the fatigue fracture mechanism of SMAs.

In Situ Observation of Effects of Stress Induced Martensitic Transformation on Fatigue Behavior in Niti Shape Memory Alloy

Stabilization of deformed stress-induced martensite and its effect on shape memory effect in an Fe-Mn-Si-Ni-Co alloy

In Situ Study of Evolution of Stress-Induced Martensitic Transformation in TiNi Shape Memory Alloy During Cyclic Deformation

Effect of Thermomechanical Coupling on Stress-Induced Martensitic Transformation Around the Crack Tip of Edge Cracked Shape Memory Alloy

Fatigue Crack Propagation Behavior of Tini50.6 Shape Memory Alloy

Stress-Induced Martensitic Transformation and Microstructure of A Ti36ni49hf15 High-Temperature Shape-Memory Alloy

Time-Dependent Deformation Behavior of TiNi Shape-Memory Alloy

Effect of the Thermomechanical Coupling on Fatigue Crack Propagation in NiTi Shape Memory Alloys

Study of Residual Stress Accumulation in Tini Shape Memory Alloy During Fatigue Using Ebsd Technique

The Microstructure and Martensitic Transformation Behaviors in Ti-Ni-Hf -X (ag, Sn) High Temperature Shape Memory Alloys

Investigation on the Deformation of TiNi Shape Memory Alloy with a Crack Using Moiré Interferometry

Finite Element Simulation of the Influence of TiC Inclusions on the Fatigue Behavior of NiTi Shape-Memory Alloys

On the Formation of Martensite in Front of Cracks in Pseudoelastic Shape Memory Alloys

Quantification of Microscale Factors for Fatigue Failure in NiTi Shape Memory Alloys

One-dimensional modeling of stress-induced transformation behaviour of shape memory alloy

Effects of triaxial stress on martensite transformation, stress–strain and failure behavior in front of crack tips in shape memory alloy NiTi

Constrained Martensitic Transformation in an in Situ Lamella TiNi/NbTi Shape Memory Composite

A Brief Study on the Fatigue of NiTi Shape Memory Alloys

Experimental and theoretical investigation of the frequency effect on low cycle fatigue of shape memory alloys

Role of Stress-Induced Martensite on Damage Behavior in a Metastable Titanium Alloy

Experimental Investigation on the Mechanical Instability of Superelastic NiTi Shape Memory Alloy