INHIBITION EFFECT OF LITHIUM NITRATE ON CARBON STEEL CORROSION IN HIGH CONCENTRATION LITHIUM BROMIDE SOLUTION AT 173°C

郭建伟,梁成浩

DOI: https://doi.org/10.3969/j.issn.1002-6495.2002.04.003

2002-01-01

Abstract:By means of electrochemical measurements and chemical immersion experiments,this paper investigates the inhibition effect of lithium nitrate on corrosion of carbon steel in 65%LiBr +0.07mol/L LiOH solution at 173℃.The results show that,the corrosion rate of carbon steel decreases with increase of LiNO 3 concentration.Combined with 150 mg/L Na 2MoO 4 in this solution,the corrosion rate shows a minimum at 100mg/L LiNO 3.Through calculation of the equilibrium potentials of the reduction electrodes for NO - 3 and MoO 2- 4,it is revealed that NO - 3 possessed higher reduction electrode potential,therewith,NO - 3 was reduced firstly,which is favior to the formation of an inner film with ferric oxide as its main component.In addition,an oxygen-deficient MoO 2 as outer-layer is formed by reduction of MoO 2- 4 when LiNO 3 is less than 100 mg/L,and then a stable double film is built up.However,when LiNO 3 is more than 100 mg/L,NO - 3 reacts with MoO 3 preferentially and results in Br - coupling in the formed passive film,which further damages the double film and thus increases the corrosion rate to a large extent.